One of the prevailing problems for materials produced by powder metallurgy is contamination from various sources. This work deals with the influence of process parameters and presence of process control agents (PCA) on the contamination level of materials produced by means of mechanical alloying (MA) technology, densified with spark plasma sintering (SPS). The equiatomic CoCrFeNi high-entropy alloy (HEA) was manufactured by the said methodology. For clear comparison, the 316L austenitic steel powder was milled and densified with identical conditions as a reference material. Both materials were milled in argon and nitrogen atmospheres for various times from 5 to 30 h. Chemical analysis of contamination by carbon, oxygen, and nitrogen within the powder and bulk materials was carried out using combustion analyzers. The microstructural analysis of powders and bulk samples was carried out using scanning electron microscopy (SEM) with focus on contaminant phases. The results show that carbon contamination increases with milling time. It is caused by wear of milling vial and balls made from high-carbon steels. Increase of carbon content within consolidation using SPS was also observed. The oxygen contamination also increases with milling time. It is more pronounced in the CoCrFeNi alloy due to higher oxidation of powder surfaces prior to milling. Milling of powders using nitrogen atmosphere also causes an increase of nitrogen content in both HEA and AISI 316L. The use of PCA (ethanol) during milling even for a short time (30 min) causes significant increase of carbon and oxygen contamination. The ways to decrease contamination are discussed in the paper.

Unconventional wire electrical discharge machining technology (WEDM) is a key machining process, especially for machining newly emerging materials, as there are almost no restrictions (only at least minimal electrical conductivity) in terms of demands on the mechanical properties of the workpiece or the need to develop new tool geometry. This study is the first to present an analysis of the machinability of newly developed high entropy alloys (HEAs), namely FeCoCrMnNi and FeCoCrMnNiC_0.2, using WEDM. The aim of this study was to find the optimal setting of machine parameters for the efficient production of parts with the required surface quality without defects. For this reason, an extensive design of experiments consisting of 66 rounds was performed, which took into account the influence of five input factors in the form of pulse off time, gap voltage, discharge current, pulse on time, and wire speed on cutting speed and the quality of the machined surface and its subsurface layer. The analysis of topography, morphology, subsurface layers, chemical composition analysis (EDX), and lamella analysis using a transmission electron microscope (TEM) were performed. An optimal setting of the machine parameters was found, which enables machining of FeCoCrMnNi and FeCoCrMnNiC_0.2 with the required surface quality without defects.

Prototypes and small series production of metal thin-walled components is a field for the use of a number of additive technologies. This method has certain limits related to the size and price of the parts, productivity, or the type of requested material. On the other hand, conventional production methods encounter the limits of shape, which are currently associated with the implementation of optimization methods such as topological optimization or generative design. An effective solution is employing hybrid technology, which combines the advantages of 3D model printing and conventional casting production methods. This paper describes the design of aluminum casting using topological optimization and technological co-design for the purpose of switching to new manufacturing technology. It characterizes the requirements of hybrid technology for the material and properties of the model in relation to the production operations of the investment casting technology. Optical roughness measurement compares the surface quality in a standard wax model and a model obtained by additive manufacturing (AM) of polymethyl methacrylate (PMMA) using the binder jetting method. The surface quality results of the 3D printed model evaluated by measuring the surface roughness are lower than for the standard wax model; however, they still meet the requirements of prototype production technology. The measurements proved that the PMMA model has half the thermal expansion in the measured interval compared to the wax model, which was confirmed by minimal shape deviations in the dimensional analysis.

The effect of phase composition and morphology on high-temperature strength in the compression of Fe-Al-Si-based iron aluminides manufactured by casting was investigated. The structure and high-temperature strength in the compression of three alloys—Fe28Al5Si, Fe28Al5Si2Mo, and Fe28Al5Si2Ti—were studied. Long-term (at 800 °C for 100 h) annealing was performed for the achievement of structural stability. The phase composition and grain size of alloys were primarily described by means of scanning electron microscopy equipped with energy dispersive analysis and Electron Backscatter Diffraction (EBSD). The phase composition was verified by X-ray diffraction (XRD) analysis. The effect of Mo and Ti addition as well as the effect of long-term annealing on high-temperature yield stress in compression were investigated. Both additives—Mo and Ti—affected the yield stress values positively. Long-term annealing of Fe28Al5Si-X iron aluminide alloyed with Mo and Ti deteriorates yield stress values slightly due to grain coarsening.

Influence of Compound Deoxidation of Steel with Al, Zr, Rare Earth Metals, and Ti on Properties of Heavy Castings: Heavy steel castings deoxidized with aluminium are sometimes brittle intercrystalline failed during their service along primary grain boundaries what is initiated by aluminium nitrides and so called conchoidal fractures are formed. The tendency to forming the conchoidal fractures depends in particular on cooling rate (the casting modulus), aluminium and nitrogen contents in steel. During deoxidation, when manufacturing heavy castings, the elements with high affinity to nitrogen, zirconium or titanium, are added to steel that would decrease nitrogen activity by the bond on stable nitrides. The formation of stable nitrides should reduce the tendency of steel to the formation of conchoidal fractures. Deoxidation was thermodynamically analyzed at presence of the mentioned elements. For particular conditions a probable course of deoxidation was estimated at test castings. The deoxidation course was checked by microanalysis of deoxidation products (inclusions). For service and experimental castings the anticipated composition of inclusions was compared. It has been proved that in heavy castings with high aluminium contents in steel under studied conditions neither the addition of zirconium nor of titanium nor of rare earth metals will prevent the formation of conchoidal fractures.