Doping with heteroatoms is the main method used to enhance energy storage with carbon materials, and polyatomic doping is one of the main challenges. Hydrothermal carbonization of cellulose was performed at 240 °C for 1 h. Ammonium sulfate and thiourea dopants were selected as the sources of inorganic nitrogen and organic nitrogen in the preparation of supercapacitor carbon. The effects of boric acid on the properties of the resulting hydrochar after KOH activation were examined. The results showed that the proportion of functional groups and the specific surface area of the activated hydrochar were reduced by the addition of boric acid, and the formation of micropores was inhibited. The hydrochar obtained from the reaction of cellulose and organic nitrogen compounds had a better pore size distribution and electrochemical properties after activation. The largest specific surface area (952.27 m²/g) was obtained when thiourea was used as the sole dopant. In a three-electrode system, the specific capacitance of the activated hydrochar reached 235.8 F/g at a current density of 1 A/g. After 20,000 charging and discharging cycles at a current density of 10 A/g, the capacitance retention rate was 99.96%. Therefore, this study showed that supercapacitor carbon with good electrochemical properties was obtained by the direct reactions of cellulose with organic nitrogen compounds.

Hydrothermal carbonization of cellulose was examined at 240 ℃ for 1 h. Ammonium sulfate and thiourea were selected as the doping sources of inorganic nitrogen and organic nitrogen for the preparation of supercapacitor carbon. The effect of boric acid on the properties of the resulting hydrochar after KOH activation was examined. The results showed that the proportion of functional groups and the specific surface area of the activated hydrochar would be reduced after the addition of boric acid, and the pore-forming process of the micropores would be inhibited. The hydrochar obtained from the reaction of cellulose and organic nitrogen compounds had better pore size distribution and electrochemical properties after activation. The largest specific surface area (952.27 m2 g-1) was obtained when only thiourea was used as the only doping source. In the three-electrode system, the specific capacitance resulting activated hydrochar reached 236.25 F g-1 at a current density of 1 A g-1. After 20,000 cycles of charging and discharging at a current density of 10 A g-1, the capacitance retention rate reached 99.96%. Therefore, this study proves that the supercapacitor carbon with good electrochemical properties could be obtained by the direct reaction of cellulose with organic nitrogen compounds.