We report highly birefringent fiber Bragg gratings in standard single-mode optical fiber realized with UV femtosecond pulses and line-by-line inscription. By controlling the three-dimensional positioning of the focused laser beam with respect to the fiber core, we achieve very high birefringence at the grating location in a single exposure. A maximum birefringence value of $7.93\times {10}^{-4}$ has been reached for 10th-order gratings when using 2 μJ pulses, which is to our knowledge the highest birefringence value reported so far. This birefringence results from UV-induced high-densification lines shifted from the center of the core, increasing the asymmetry of the induced-stress lines. With a Bragg wavelength spacing reaching more than 800 pm between polarization modes, such gratings are particularly well suited for selective filtering or, as demonstrated here, for temperature-insensitive transverse-strain measurements.

Instrumentation techniques, implementation and installation methods are major concerns in today’s distributed and quasi-distributed monitoring applications using fiber optic sensors. Although many successful traffic monitoring experiments have been reported using Fiber Bragg Gratings (FBGs), there has been no standardized solution proposed so far to have FBG seamlessly implemented in roads. In this work, we investigate a mobile platform including FBG sensors that can be positioned on roads for the purpose of vehicle speed measurements. The experimental results prove the efficiency of the proposed platform, providing a perspective toward weigh-in-motion systems.

Bare and gold-coated tilted fiber Bragg gratings (TFBGs) can nowadays be considered as a mature technology for volume and surface refractometric sensing, respectively. As for other technologies, a continuous effort is made towards the production of even more sensitive sensors, thereby enabling a high-resolution screening of the surroundings and the possible detection of rare events. To this aim, we study in this work the development of TFBG refractometers in 4-core fibers. In particular, we show that the refractometric sensitivity of the cut-off mode can reach 100 nm/RIU for a bare grating. Using another demodulation method, a tenfold sensitivity increase is obtained when tracking the extremum of the SPR (surface plasmon resonance) envelope for a gold-coated TFBG configuration. Immobilization of DNA probes was performed as a proof-of-concept to assess the high surface sensitivity of the device.

New dual temperature and strain sensor has been designed using eccentric second-order fiber Bragg gratings produced in standard single-mode optical fiber by point-by-point direct writing technique with tight focusing of 800 nm femtosecond laser pulses. With thin gold coating at the grating location, we experimentally show that such gratings exhibit a transmitted amplitude spectrum composed by the Bragg and cladding modes resonances that extend in a wide spectral range exceeding one octave. An overlapping of the first order and second order spectrum is then observed. High-order cladding modes belonging to the first order Bragg resonance coupling are close to the second order Bragg resonance, they show a negative axial strain sensitivity (−0.55 pm/με) compared to the Bragg resonance (1.20 pm/με) and the same temperature sensitivity (10.6 pm/°C). With this well conditioned system, temperature and strain can be determined independently with high sensitivity, in a wavelength range limited to a few nanometers.

Fiber Bragg gratings (FBGs) in cyclic transparent fluoropolymer (CYTOP) optical fiber are the subject of a lot of research as they can be of interest for many applications, such as temperature, humidity, strain, and radiation sensing. We report here a new technique to produce high quality FBGs in CYTOP fiber. It uses a femtosecond laser system operating at 400 nm and a phase mask. In contrast to previously reported results, the gratings are obtained in a few seconds with a writing power as low as 80 μW. With this setup, 2 mm-long gratings with reflectivity up to 92 % and full width at half maximum bandwidth around 0.5 nm were obtained in less than 10 s. The resonance wavelengths of the FBGs are confirmed by numerical computation in the graded-index multimode CYTOP fiber, and the mode selection characteristic of FBGs in CYTOP is investigated. Finally, the temperature sensitivity of CYTOP FBG is measured in different mode groups for heating up and cooling down, showing values independent of the mode group measured, but with a small hysteresis.

We report the inscription of highly reflective fiber Bragg gratings in perfluorinated polymer (CYTOP) optical fibers using 800 nm femtosecond pulses and a line-by-line inscription method. We demonstrate that the energy for grating inscription without damage is below 27 nJ. After the writing process, we show that the grating reflectivity continues to rise for several hours. The obtained gratings show reflectivity degradation with temperature increase, while the Bragg wavelength undergoes a linear temperature dependence of 37.7 pm/°C when the humidity is controlled and the heating/cooling rate is relatively low ( ≤ 0.14 ∘ C / m i n ). The humidity sensitivity at a fixed temperature (25°C) is 22.3 pm/%RH. Finally, the axial strain sensitivity is determined to be 1.35 pm/µɛ.