Biomass renewable energy has become a major target of the Thailand Alternative Energy Development Plan (AEDP) since the country’s economy is largely based on agricultural production. Rice husk (RH) is one of the most common agricultural residues in Thailand. This research aims to investigate yields and properties of biochar produced from copyrolysis of RH and plastic (high-density polyethylene (HDPE)) at different ratios, temperatures, and holding times. For both individual and copyrolysis, the temperature variation generated more pronounced effects than the holding time variation on both biochar yields and properties. For individual pyrolysis of RH, the maximum biochar yield of ∼54 wt % was obtained at 400 °C. A shift in temperature from 400 to 600 °C resulted in RH biochars with higher fixed carbon (FC) and carbon (C) contents by ∼1.11–1.28 and 1.06–1.22 times, respectively, while undetectable changes in higher heating values (HHVs) were noticed. For copyrolysis, obvious negative synergistic effects were observed due to the radical interaction between the rich H content of HDPE and RH biochars, which resulted in lower biochar yields as compared to the theoretical estimation based on individual pyrolysis values. However, the addition of HDPE positively impacted the FC and C contents, especially when 10 and 20 wt % HDPE were added to the feedstock. Besides, higher HDPE blending ratios resulted in biochars with improved HHVs, and >1.5 times improvement in HHV was reported in the biochar with 50 wt % HDPE addition in comparison with RH biochar obtained under the same conditions. In summary, biochars generated in this study have the potential to be utilized as a solid fuel or soil amendment.

Potassium (K) has been recognized as an essential element in intensive agricultural production systems, and deficiency of K usually results in a decrease in crop yields. The utilization of potassium-solubilizing bacteria (KSB) to increase the soluble K content in soil has been regarded as a desirable pathway to increase plant yields. Following the inoculation of KSB in the soil, potassium can be released (in the form of K⁺) and consumed by plants. This study aims to investigate and compare the distribution characteristics of potassium-solubilizing bacteria between forest and plantation soils in Myanmar. In this study, 14 KSB strains were isolated from rhizosphere samples collected from forest soil, as well as fertilized rubber tree rhizosphere soil and fertilized bare soil from a plantation. Broadleaf forests with high levels of canopy cover mainly comprised the forest environment, and rubber trees were planted in the plantation environment. The Chao and abundance-based coverage estimator (ACE) indices showed that the microbial abundance of the plantation soil was higher than that of the forest soil. According to the Illumina MiSeq sequencing analysis results, the Shannon index of the forest soil was lower while the Simpson index was higher, which demonstrated that the microbial diversity of the forest soil was higher than that of the plantation soil. Potassium-solubilizing test results showed that the strains E, I, M, and N were the most effective KSB under liquid cultivation conditions. Additionally, KSB only accounted for less than 5.47% of the total bacteria detected in either of the sample types, and the distribution of dominant KSB varied with the soil samples. As another result, the abundance of Pseudomonas spp. in S1 was higher than in S2 and S3, indicating a negative impact on the growth of Pseudomonas in the fertilized rubber tree rhizosphere soil. The significance of our research is that it proves that the increasing use of KSB for restoring soil is a good way to reduce the use of chemical fertilizers, which could further provide a relatively stable environment for plant growth.

Humins, waste from biomass hydrolysis, are the main factor limiting the utilization efficiency of biomass carbon. In the present study, waste humins were employed for activated carbon production though KOH activation in a temperature range of 500–900 °C. The structure and properties of the activated carbons were studied, and a honeycomb-like macropore structure was observed. High activation temperature was demonstrated to be capable of promoting the formation of activated carbon with high surface area, high pore volume and high adsorption capacity. The activated carbon obtained by carbonization at 800 °C (KOH800) was selected as sorbent to adsorb methylene blue (MB) and phenol in aqueous solution, and the adsorption process can be explained by pseudo-second-order kinetic model. The adsorption behavior complies with Langmuir isotherm model and exhibits superior adsorption capacity of 1195 and 218 mg/g for MB and phenol, respectively. The impacts of surface area, acidic active sites and pore structures were also investigated, and it was found that the adsorption of approximately 44.0% MB and 39.7% phenol were contributed by the pores with apertures from 1.7 nm to 300 nm.

Humins are low-value-added byproducts from the biomass acid hydrolysis process. In the present work, humins were first employed as a phenol replacement for synthesis of modified phenol-formaldehyde adhesives through a two-step process. In this process, humins were first utilized to obtain alkaline soluble products, mainly consisting of phenolics, through a hydrothermal process. The obtained alkaline soluble products then reacted with phenol and formaldehyde to produce humin-phenol-formaldehyde adhesive (HPFA). The physicochemical properties of HPFA, including viscosity, bonding strength, pH, free formaldehyde level, free phenol level and solid content, met the requirements of the GB/T 14732-2006 Chinese National Standard.