Background: Fungi growing on wood cause deterioration of stored food materials or discoloration of the wood itself, and the search for new and safe bioagents is recently needed. Methods: Essential oils (EOs) from aerial parts from Mentha longifolia L. and Citrus reticulata L., analyzed by gas chromatography-mass spectrometry (GC-MS), were tested for their antifungal activity by the vapor method against four common fungi, Aspergillus flavus, A. niger, A. fumigatus, and Fusarium culmorum, and confirmed by SEM examination as the oils applied on wood samples. Results: The most abundant compounds identified in the EO from M. longifolia were menthone and eucalyptol; in C. reticulata EO, they were β-caryophyllene, β-caryophyllene oxide, and β-elemene. EOs from M. longifolia and C. reticulata, at 500 and 250 µL/mL, showed potent antifungal activity against A. flavus and A. fumigatus, with 100% fungal mycelial inhibition growth (FMIG). C. reticulata and M. longifolia EOs, at 125 µL/mL, observed FMIG values of 98% and 95%, respectively, against A. fumigatus. M. longifolia EO, at 500 and 250 µL/mL, showed potent activity against A. niger, with 100% FMIG. F. culmorum completely inhibited (100% FMIG) EOs from M. longifolia and C. reticulata applied at 500 µL/mL. Pinus roxburghii Sarg. Wood, treated with M. longifolia at 125 µL/mL, showed inhibition zone values of 7.33 and 21.33 mm against A. flavus and A. niger, respectively. Conclusions: Both oils possessed good wood-biofungicide activity with the vapor method, as clearly shown by the SEM examination. These activities suggest their possible use as natural wood preservatives.

In the present study, novel mixed additives of Chitosan or Paraloid B-72 combined with nanoparticles (NPs) of Ag, ZnO, or cellulose (NCL) were examined for their effects on the mechanical, optical, and fungal inhibition properties of the papersheets produced. The highest tensile, tear, and burst indices of the papersheets were observed for flax pulp treated with additives of Paraloid B-72 + ZnO NP (1%), Chitosan + ZnO NP (3%), and Chitosan + NCL (3%) at levels of 59.93 N·m/g, 18.45 mN·m²/g, and 6.47 kPa·m²/g, respectively. Chitosan + ZnO NP (1%) added to flax pulp showed the highest fungal mycelial inhibition (FMI) (1.85%) against Aspergillus flavus. Chitosan + Ag NP (1%) exhibited the highest FMI percentage (11.48%) when added to pulp against A. terreus. Pulp treated with Paraloid B-72 + Ag NP (1%) exhibited the highest activity against Stemphylium solani with an FMI value of 3.7%. The results indicate that the technological properties of the papersheets were enhanced with the addition of novel mixtures to the pulp.

In the present work, sheets of Papyrus (Cyperus papyrus L.), manufactured by lamination from strips pre-treated with different treatments, were evaluated for their technological and fungal infestation properties (Aspergillus flavus AFl375, A. niger Ani245 and Colletotrichum gloeosporioides Cgl311). The results showed that the highest values of tensile strength, tear strength, burst index and double-fold number were observed in papyrus sheets produced from strips treated with nano-cellulose (0.25%), dimethyl sulfoxide (DMSO 10%), Tylose (0.25%) and nano-cellulose (0.5%), with values of 98.90 N·m/g, 2343.67 mN·m²/g, 1162 kpa·m²/g and 8.33, respectively. The percentage of brightness ranged from 49.7% (strips treated with KOH 2% + 100 mL NaClO) to 9.6% (strips treated with Eucalyptus camaldulensis bark extract 2%), while the percentage of darkness ranged from 99.86% (strips treated with Salix babylonica leaf extract 2% or E. camaldulensis bark extract 0.5%) to 67.26% (strips treated with NaOH (2%) + 100 mL NaClO). From the SEM examination, sheets produced from treated strips with extracts from P. rigida and E. camaldulensis or S. babylonica showed no growths of A. flavus and C. gloeosporioides. Additionally, other pre-treatments, such as Nano-cellulose+Tylose 0.5% (1:1 v/v) and Tylose 0.5%, were also found to have no growth of A. niger. In conclusion, strips pre-treated with nanomaterials and extracts were enhanced in terms of the technological and antifungal properties of produced Papyrus sheets, respectively.

In the pulp and paper industry, several studies have been done to improve and enhance the properties of the mechanical, optical, and antimicrobial activities of pulp produced with different additives. In the present study, pulp of wood branches (WBs) from Eucalyptus camaldulensis Dehnh. and Meryta sinclairii (Hook.f.) Seem. was treated with n-hexane oily extracts (HeOE) from Melia azedarach L. fruits, Magnolia grandiflora L. leaves, and Sinapis alba L. seeds as additives at concentrations of 1%, 3%, and 5% based on oven-dry pulp weight. Measured mechanical properties were higher in paper sheets made from E. camaldulensis than M. sinclairii WB pulp. The highest tensile index values were observed with E. camaldulensis WB pulp treated with 5% HeOEs of S. alba (33.90 N·m/g) and M. grandiflora (33.76 N·m/g) compared to control (32.10 N·m/g); the highest tear index with 5% HeOE of S. alba (4.11 mN·m²/g) compared to control (3.32 mN·m²/g); and the highest burst index with 5% HeOE of S. alba (4.11 kPa·m²/g) compared to control (3.08 kPa·m²/g). The highest double-fold number value (9) was observed with E. camaldulensis WB pulp treated with 5% HeOEs of S. alba, M. azedarach, and M. grandiflora but with no significant difference compared to control treatment (8.33) or other HeOE treatments with E. camaldulensis WB pulp. Scanning electron microscope (SEM) examination showed clear inhibition of the growth of Aspergillus terreus with WB pulp paper discs of E. camaldulensis and M. sinclairii treated with HeOEs of M. azedarach, S. alba, and M. grandiflora at 3% and 5% compared to control treatment, while HeOEs at 5% concentration showed no growth of A. niger and A. terreus. The present findings establish that the HeOEs from M. azedarach, S. alba, and M. grandiflora at 3% and 5% are novel natural products that can be used as alternatives to improve the properties and antifungal activity of WB pulp produced from E. camaldulensis and M. sinclairii.

The accelerated ageing of wood in terms of heating or iron rusting has a potential effect on the physio-mechanical, chemical and biological properties of wood. The effects of accelerated ageing on the mechanical, physical and fungal activity properties of some wood materials (Schinus terebinthifolius, Erythrina humeana, Tectona grandis, Pinus rigida and Juglans nigra) were studied after several cycles of heating and iron rusting. The fungal activity was assayed against the growth of Aspergillus terreus, Aspergillus niger, Fusarium culmorum and Stemphylium solani. In addition, the mechanical and optical properties of paper sheets produced from those wood pulps by means of Kraft cooking were evaluated. The mechanical and chemical properties of the studied wood species were affected significantly (p < 0.05) by the accelerated ageing, compared to control woods. With Fourier transform infrared (FTIR) spectroscopy, we detected an increase in the intensity of the spectra of the functional groups of cellulose in the heated samples, which indicates an increase in cellulose content and decrease in lignin content, compared to other chemical compounds. For pulp properties, woods treated by heating showed a decrease in the pulp yield. The highest significant values of tensile strength were observed in pulp paper produced from untreated, heated and iron-rusted P. rigida wood and they were 69.66, 65.66 and 68.33 N·m/g, respectively; we calculated the tear resistance from pulp paper of untreated P. rigida (8.68 mN·m²/g) and T. grandis (7.83 mN·m²/g) and rusted P. rigida (7.56 mN·m²/g) wood; we obtained the values of the burst strength of the pulp paper of untreated woods of P. rigida (8.19 kPa·m²/g) and T. grandis (7.49 kPa·m²/g), as well as the fold number of the pulp paper of untreated, heated and rusted woods from P. rigida, with values of 195.66, 186.33 and 185.66, respectively. After 14 days from the incubation, no fungal inhibition zones were observed. Accelerated ageing (heated or iron-rusted) produced significant effects on the mechanical and chemical properties of the studied wood species and affected the properties of the produced pulp paper.

Four saprophytic bacterial and fungal species attacked the manuscript that dated back to 1251 AH at Al-Azhar libraryin Cairo, Egypt were isolated. Based on the partial 16S rRNA gene sequence, the isolated bacteria were Acinetobacterindicus and Exiguobacterium aurantiacum. The fungal species were Stachybotrys chartarum and Aspergillus flavus. Acacia nilotica fruit extraction exhibited considerable antimicrobial activity at different concentrations against theisolated bacteria and fungi.