This study focus on Fourier Transform Infrared Spectroscopy (FTIR) analysis of paddy straw pulp treated using deep eutectic solvent (DES). DES was synthesized using potassium carbonate and glycerol at different molar ratio under normal atmospheric pressure. Pretreatment of lignocellulosic biomass was carried out at temperature of 120°C for 60 minutes under mass ratio of paddy straw to DES 1:9. The chemical structures of the untreated paddy straw and paddy straw pulp treated with different molar ratio of DES were analyzed using FTIR. The characterization result from FT-IR spectra indicated that the potassium carbonate-glycerol DES deconstructed the structures of paddy straw by removing lignin and hemicellulose during the pulping process. The peak intensity that occurs at region between 900 cm⁻¹ and 1500 cm⁻¹ shows that the presence of elevated level of cellulose after lignocellulosic pulping. From FT-IR analysis, DES could not remove the functional group of lignin and hemicellulose completely but yet expose the structure of cellulose.