Agricultural waste materials (strawberry seeds and pistachio shells) were used for preparation of activated carbons by two various methods. Chemical activation using acetic acid and physical activation with gaseous agents (carbon dioxide and water vapor) were chosen as mild and environmentally friendly methods. The effect of type of raw material, temperature, and activation agent on the porous structure characteristics of the materials was discussed applying various methods of analysis. The best obtained activated carbons were characterized by high values of specific surface area (555–685 m²/g). The Guinier analysis of small-angle X-ray scattering (SAXS) curves showed that a time of activation affects pore size. The samples activated using carbon dioxide were characterized mostly by the spherical morphology of pores. Adsorbents were utilized for removal of the model organic pollutants from the single- and multicomponent systems. The adsorption capacities for the 4-chloro-2-methyphenoxyacetic acid (MCPA) removal were equal to 1.43–1.56 mmol/g; however, for adsorbent from strawberry seeds it was much lower. Slight effect of crystal violet presence on the MCPA adsorption and inversely was noticed as a result of adsorption in different types of pores. For similar herbicides strong competition in capacity and adsorption rate was observed. For analysis of kinetic data various equations were used.

Metal-carbon nanocomposites possess attractive physical-chemical properties compared to their macroscopic counterparts. They are important and unique nanosystems with applications including in the future development of nanomaterial enabled sensors, polymer fillers for electromagnetic radiation shields, and catalysts for various chemical reactions. However, synthesis of these nanocomposites typically employs toxic solvents and hazardous precursors, leading to environmental and health concerns. Together with the complexity of the synthetic processes involved, it is clear that a new synthesis route is required. Herein, Cu/C, Ni/C and Co/C nanocomposites were synthesized using a two-step method including mechanochemical treatment of polyethylene glycol and acetates of copper, nickel and cobalt, followed by pyrolysis of the mixtures in an argon flow at 700 °C. Morphological and structural analysis of the synthesized nanocomposites show their core-shell nature with average crystallite sizes of 50 (Cu/C), 18 (Co/C) and 20 nm (Ni/C) respectively. The carbon shell originates from disordered sp² carbon (5.2–17.2 wt.%) with a low graphitization degree. The stability and prolonged resistance of composites to oxidation in air arise from the complete embedding of the metal core into the carbon shell together with the presence of surface oxide layer of metal nanoparticles. This approach demonstrates an environmentally friendly method of mechanochemistry for controllable synthesis of metal-carbon nanocomposites.