The important benefits of ultrafine-grained (UFG) alloys for various applications stem from their enhanced superplastic properties. However, decreasing the temperature of superplasticity and providing superplastic forming at lower temperatures and higher strain rates is still a priority. Here, we disclose, for the first time, the mechanism by which grain boundary sliding and rotation are enhanced, when UFG materials have grain boundary segregation of specific alloying elements. Such an approach enables achieving superplasticity in commercial Al alloys at ultralow homologous temperatures below 0.5 (i.e. below 200°C), which is important for developing new efficient technologies for manufacturing complex-shaped metallic parts with enhanced service properties. IMPACT STATEMENT For the first time, ultralow-temperature superplasticity is found in commercial 7xxx Al alloy. This discovery enables the development of new technologies for the superplastic forming of complex-shaped products with enhanced service properties.

An ultrafine-grained (UFG) Al-4.8%Zn-1.2%Mg-0.14%Zr (wt%) alloy was processed by high pressure torsion (HPT) technique and then aged at 120 and 170 °C for 2 h. The changes in the microstructure due to this artificial aging were studied by X-ray diffraction and transmission electron microscopy. It was found that the HPT-processed alloy has a small grain size of about 200 nm and a high dislocation density of about 8 × 10¹⁴ m⁻². The majority of precipitates after HPT are Guinier–Preston (GP) zones with a size of ~ 2 nm, and only a few large particles were formed at the grain boundaries. Annealing at 120 and 170 °C for 2 h resulted in the formation of stable MgZn₂ precipitates from a part of the GP zones. It was found that for the higher temperature the fraction of the MgZn₂ phase was larger and the dislocation density in the Al matrix was lower. The changes in the precipitates and the dislocation density due to aging were correlated to the hardness evolution. It was found that the majority of hardness reduction during aging was caused by the annihilation of dislocations and some grain growth at 170 °C. The aging effect on the microstructure and the hardness of the HPT-processed specimen was compared to that observed for the UFG sample processed by equal-channel angular pressing. It was revealed that in the HPT sample less secondary phase particles formed in the grain boundaries, and the higher amount of precipitates in the grain interiors resulted in a higher hardness even after aging.

This study aims to achieve an ultrafine-grained (UFG) Al 2024 alloy superplasticity at temperatures lower than the traditional ones for commercial Al alloys (400–500 °C). The UFG structure with a mean grain size of 100 nm produced in the alloy by high-pressure torsion at room temperature provided a very high strength—microhardness (HV_0.1) of 286 ± 4, offset yield strength (σ_0.2) of 828 ± 9 MPa, and ultimate tensile strength (σ_UTS) of 871 ± 6 MPa at elongation to failure (δ) of 7 ± 0.2%. Complex tensile tests were performed at temperatures from 190 to 270 °C and strain rates from 10⁻² to 5 × 10⁻⁵ s⁻¹, and the values of flow stress, total elongation and strain rate-sensitivity coefficient were determined. The UFG alloy was shown to exhibit superplastic behavior at test temperatures of 240 and 270 °C. For the first time, 400% elongation was achieved in the alloy at an unusually low temperature of 270 °C (0.56 T_m) and strain rate of 10⁻³ s⁻¹. The UFG 2024 alloy after superplastic deformation was found to have higher strength (150–160 HV) than that after the standard strengthening heat treatment T6.

The last two decades have witnessed significant progress in the development of severe plastic deformation techniques to produce ultrafine-grained materials with new and superior properties. This review examines works and achievements related to the low-temperature superplasticity of ultrafine-grained aluminum alloys. The examples are provided of the possibility to observe low-temperature superplasticity in aluminum alloys at temperatures less than 0.5 T_melt and even at room temperature, and herein, we demonstrate the cases of achieving high ductility and high strength in aluminum alloys from processing utilizing severe plastic deformation. Special emphasis is placed on recent studies of the formation of segregations of alloying elements at grain boundaries in UFG Al alloys and their influence on the development of grain boundary sliding and manifestation of low-temperature superplasticity. In addition, the current status and innovative potential of low-temperature superplasticity in aluminum alloys are observed.