Metal oxide nanoparticles synthesized by the biological method represent the most recent research in nanotechnology. This study reports the rapid and ecofriendly approach for the synthesis of CeO₂ nanoparticles mediated using the Abelmoschus esculentus extract. The medicinal plant extract acts as both a reducing and stabilizing agent. The characterization of CeO₂ NPs was performed by scanning electron microscopy (SEM), X-ray diffraction (XRD), ultraviolet-visible spectroscopy (UV-Vis), and Fourier transform infrared spectroscopy (FTIR). The in vitro cytotoxicity of green synthesized CeO₂ was assessed against cervical cancerous cells (HeLa). The exposure of CeO₂ to HeLa cells at 10–125 µg/mL caused a loss in cellular viability against cervical cancerous cells in a dose-dependent manner. The antibacterial activity of the CeO₂ was assessed against S. aureus and K. pneumonia. A significant improvement in wound-healing progression was observed when cerium oxide nanoparticles were incorporated into the chitosan hydrogel membrane as a wound dressing.

This study explores the impact of Cu and Ni doping on the structural, wettability, optical, and photocatalytic properties of ZnO thin films. The co-doped thin films, with varying Ni concentrations, were deposited using a spray pyrolysis method onto pre-heated soda lime glass substrates. X-ray diffraction analysis confirmed the hexagonal wurtzite structure with preferred orientation primarily along the (002) plane, while crystallinity decreased with higher Ni concentrations. Scanning electron microscopy reveals a compact, adherent structure in all films, with Ni incorporation altering the surface morphology. Fourier transform infrared spectroscopy identified characteristic absorption bands for metal-oxygen bonds. Optical analysis indicated that all thin films exhibited over 88% average transmittance in the visible region, accompanied by a red shift in the optical bandgap. Photoluminescence spectra exhibited a broad emission band in the visible region, indicating intrinsic and extrinsic defects induced by doping. Co-doping transforms the wettability character of ZnO thin films from hydrophilic to hydrophobic. Finally, the photodegradation efficiency of the thin films against methylene blue under sunlight significantly increases from 72% to 92% with an increase in Ni concentration.