Hydroxyapatite (HAP) has excellent biocompatibility with living bone tissue and does not cause defensive body reactions, therefore, it has become one of the most widely used calcium phosphate materials in dental and medical fields. However, its poor mechanical properties have been a substantial challenge in the application of HAP for the replacement of load-bearing or large bone defects. Laminated HAP–45S5 bioglass ceramics composites were prepared by the spark plasma sintering (SPS) technique. The interface structures between the HAP and 45S5 bioglass layers and the mechanical properties of the laminated composites were investigated. It was demonstrated that there was mutual transfer and exchange of Ca and Na atoms at the interface between 45S5 bioglass/HAP laminated layers, which contributed considerably to the interfacial bonding. Due from the laminated structure and strong interface bonding, laminated HAP–45S5 bioglass is recommended for structural applications.

Hydroxyapatite (HAP) displays a high degree of similarity to the inorganic components that make up roughly 70% of human hard tissue, and it possesses exceptional biological activity and biocompatibility. It is currently internationally recognized as the most biologically active hard tissue implant material. However, its substandard mechanical properties have significantly limited the application of HAP in areas requiring load bearing or in the repair of large bone defects. In this study, HAP/45S5 bioglass laminated ceramic composites were consolidated using the spark plasma sintering (SPS) technique. The grain growth and phase transformation of HAP and 45S5 bioglass were examined at various sintering temperatures. The mechanical properties of the laminated composites were investigated. At 950 °C, the flexural strength and fracture work of the sintered body were (153.22 ± 7.7) MPa and (2049 ± 34) J·m⁻², respectively. These results corresponded to the load–displacement curves and showed that the composites met the mechanical performance requirements of the support material.