In this paper, in order to increase the power conversion efficiency we demonstrated the selective growth of “nanoforest” composed of high density, long branched “treelike” multigeneration hierarchical ZnO nanowire photoanodes. The overall light-conversion efficiency of the branched ZnO nanowire DSSCs was almost 5 times higher than the efficiency of DSSCs constructed by upstanding ZnO nanowires. The efficiency increase is due to greatly enhanced surface area for higher dye loading and light harvesting, and also due to reduced charge recombination by providing direct conduction pathways along the crystalline ZnO “nanotree” multi generation branches. We performed a parametric study to determine optimum hierarchical ZnO nanowire photoanodes through the combination of both length-wise growth and branched growth processes. The novel selective hierarchical growth approach represents a low cost, all solution processed hydrothermal method that yields complex hierarchical ZnO nanowire photoanodes by utilizing a simple engineering of seed particles and capping polymer.

For the realization of high-efficiency flexible optoelectronic devices, transparent electrodes should be fabricated through a low-temperature process and have the crucial feature of low surface roughness. In this paper, we demonstrated a two-step spray-coating method for producing large-scale, smooth and flexible silver nanowire (AgNW)–poly3,4-ethylenedioxythiophene:polystyrenesulfonate (PEDOT:PSS) composite electrodes. Without the high-temperature annealing process, the conductivity of the composite film was improved via the lamination of highly conductive PEDOT:PSS modified by dimethyl sulfoxide (DMSO). Under the room temperature process condition, we fabricated the AgNW–PEDOT:PSS composite film showing an 84.3% mean optical transmittance with a 10.76 Ω sq⁻¹ sheet resistance. The figure of merit Φ_TC was higher than that obtained from the indium tin oxide (ITO) films. The sheet resistance of the composite film slightly increased less than 5.3% during 200 cycles of tensile and compression folding, displaying good electromechanical flexibility for use in flexible optoelectronic applications.