Micro milling is widely used to manufacture micro parts due to its obvious advantages. The minimum undeformed chip thickness, the effective rake angle, and size effect are the typical characteristics and closely related to each other in micro milling. In this paper, the averaging method is proposed to quantitatively estimate the effective rake angle in the cutting process. The minimum undeformed chip thickness is explained based on the effective rake angle and determined to be 0.17 r_n (tool cutting edge radius). Then, micro milling experiment was conducted to study the effect of the minimum undeformed chip thickness. It is found that the minimum undeformed chip thickness results in the unstable cutting process, the uneven peaks on cutting force signal, and the dense characteristic frequency distribution on frequency domain signal. The dominant ploughing effect induces the great specific cutting energy and the deteriorated surface roughness due to the minimum undeformed chip thickness.

Cemented carbide is currently used for various precise molds and wear resistant parts. However, the machining of cemented carbide still is a difficult challenge due to its superior mechanical properties. In this paper, an experimental study was conducted on direct micro milling of cemented carbide with a polycrystalline diamond (PCD) micro end mill. The cutting force characteristics, surface formation, and tool wear mechanisms were systematically investigated. Experimental results show that cemented carbide can be removed with ductile cutting utilizing the PCD tool with a large tool tip radius. Micro burrs, brittle pits, and cracks are the observed surface damage mechanisms. The tool wear process presents microchipping on the cutting edge and exfoliating on the rake face in the early stage, and then severe abrasive and adhesive wear on the bottom face in the following stage.

The burr on micro part has harmful effect on the dimensional accuracy and service performance. The original control of exit burr formation during micro milling is desirable and advisable. In this paper, the formation mechanism of exit burr was studied based on the varying cutting direction during micro milling. Three exit burr control strategies were concluded, the material properties embrittlement, the support stiffness increasing and machining parameter optimizing operations. Then, micro milling experiments were carried out to investigate the exit burr morphology and size. It was found that the exit burr formation was attributed to the change of material flowing path at the exit surface, which was caused by the negative shear deformation zone that was induced by the discontinuous shape features. Different exit burr morphologies were classified; the triangle exit burr type was caused by the varying exit burr growing direction along the exit surface. The optimal machining parameters in micro milling to obtain a small exit burr were suggested.