Self-assembled nanolayering structures have been reported in resin-dentin interfaces created by adhesives that contain 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP). These structures have been hypothesized to contribute to bond durability. The objective of the present study was to determine the extent of nanolayering in resin-dentin interfaces after application of commercialized 10-MDP-containing self-etch and universal adhesives to human dentin. Seven commercialized adhesives were examined: Adhese Universal (Ivoclar-Vivadent), All-Bond Universal (Bisco, Inc.), Clearfil SE Bond 2, Clearfil S3 Bond Plus, Clearfil Universal Bond (all from Kuraray Noritake Dental Inc.), G-Premio Bond (GC Corp.), and Scotchbond Universal (3M ESPE). Each adhesive was applied in the self-etch mode on midcoronal dentin according to the respective manufacturer’s instructions. Bonded specimens (n = 6) were covered with flowable resin composite, processed for transmission electron microscopy, and examined at 30 random sites without staining. Thin-film glancing angle X-ray diffraction (XRD) was used to detect the characteristic peaks exhibited by nanolayering (n = 4). The control consisted of 15%wt, 10%wt, and 5%wt 10-MDP (DM Healthcare Products, Inc.) dissolved in a mixed solvent (ethanol and water weight ratio 9:8, with photoinitiators). Experimental primers were applied to dentin for 20 s, covered with hydrophobic resin layer, and examined in the same manner. Profuse nanolayering with highly ordered periodicity (~3.7 nm wide) was observed adjacent to partially dissolved apatite crystallites in dentin treated with the 15% 10-MDP primer. Three peaks in the 2θ range of 2.40° (3.68 nm), 4.78° (1.85 nm), and 7.18° (1.23 nm) were identified from thin-film XRD. Reduction in the extent of nanolayering was observed in the 10% and 5% 10-MDP experimental primer-dentin interface along with lower intensity XRD peaks. Nanolayering and characteristic XRD peaks were rarely observed in specimens prepared from the commercialized adhesives. The sparsity of nanolayering in resin-dentin interfaces created by commercialized adhesives challenges its clinical effectiveness as a mechanism for improving bond longevity in dentin bonding.

Currently available drug delivery systems for oral diseases suffer from short retention time and poor local concentrations at the target site. A biodegradable stimulus-responsive hydrogel was synthesized in the present study to evaluate its application as an environmentally sensitive carrier for on-demand intraoral drug delivery. The hydrogel was synthesized from diacrylate-containing polyethylene glycol–based scaffolds and a cysteine-terminated peptide crosslinker (CGPQG↓IWGQC) via a Michael-type addition reaction. Because CGPQG↓IWGQC can be cleaved by matrix metalloproteinase 8 (MMP-8), minocycline hydrochloride, bovine serum albumin, or an antibacterial peptide (KSL) was incorporated into the scaffolds to evaluate the MMP-8-responsive release behavior of the on-demand drug delivery system. Hydrogel characterization and gelation kinetics were examined with gel time, Fourier-transform infrared spectroscopy, scanning electron microscopy, and measurements of rheologic parameters. Degradation behavior and MMP-8-responsive drug release were performed by high-performance liquid chromatography and protein-specific assay. Biocompatibility evaluation indicated that the hydrogels were noncytotoxic. Antibacterial testing demonstrated that the released drugs were able to maintain bioactivity. Taken together, these results suggest that the MMP-8-sensitive hydrogel is a promising candidate for on-demand intraoral localized drug delivery. Because MMP-8 is one of the most important biomarkers for periodontitis, the MMP-8-responsive hydrogel has potential to be used for in situ adaptive degradation in response to chronic periodontitis and peri-implantitis. This notion has to be tested in animal models of periodontal disease.

One of the primary causes for the failure of glass ionomer cement (GIC) is secondary caries. To enhance the anti-microbial performance of GIC without affecting its mechanical properties, chlorhexidine (CHX) was encapsulated in expanded-pore mesoporous silica nanoparticles (pMSN) to synthesize CHX@pMSN. CHX@pMSN was added at three mass fractions (1%, 5%, and 10% (w/w)) to GIC powder as the experimental groups. Pure GIC was set as the control group. The mechanical and anti-biofilm properties of GIC from each group were tested. The results demonstrated that CHX was successfully encapsulated on/into pMSN, and the encapsulating efficiency of CHX was 44.62% in CHX@pMSN. The anti-biofilm ability was significantly enhanced in all experimental groups (p < 0.001) compared with that in the control group. CHX was continuously released, and anti-biofilm ability was maintained up to 30 days. In addition, the mechanical properties (compressive strength, surface hardness, elastic modulus, water sorption, and solubility) of 1% (w/w) group were maintained compared with those in the control group (p > 0.05). In conclusion, adding 1% (w/w) CHX@pMSN to GIC led to conspicuous anti-biofilm ability and had no adverse effect on the mechanical properties of this restorative material. This study proposes a new strategy for preventing secondary caries by using CHX@pMSN-modified GIC.

Injective thermosensitive hydrogels are considered promising scaffolds to trigger dental pulp regeneration in devitalized human teeth. In this study, we developed a hydroxypropyl chitin (HPCH)/chitin whisker (CW) thermosensitive hydrogel with enhanced mechanical properties and biological activities. Exosomes can serve as biomimetic tools for tissue engineering, but the rapid clearance of unconjugated exosomes in vivo limits their therapeutic effects. To address this challenge, exosomes were isolated from human pulp stem cells (hDPSCs) and directly embedded into the HPCH/CW pre-gel to form an exosome-loaded hydrogel (HPCH/CW/Exo). The exosome-loaded thermosensitive hydrogel can be easily injected into an irregular endodontic space and gelated in situ. In vitro cell experiments proved that the delivery of exosomes significantly improved the ability of hydrogels to promote odontogenesis and angiogenesis. Meanwhile, in vivo animal experiments revealed the formation of new dental pulp-like tissues in an implanted tooth root model. Therefore, the proposed hydrogel provides a great potential alternative to traditional root canal therapy in dental clinics.