Recently, nanosilver pastes have emerged as one of the most promising high temperature bonding materials for high frequency and high power applications, which provide an effective lead-free electronic packaging solution instead of high-lead and gold-based solders. Although nanosilver pastes can be sintered at lower temperature compared to bulk silver, applications of nanosilver pastes are limited by long-term sintering time (20–30 min), relative high sintering temperature (>250 °C), and applied external pressure, which may damage chips and electronic components. Therefore, low temperature rapid sintering processes that can obtain excellent nanosilver joints are anticipated. In this regard, we present a review of recent progress in the rapid sintering of nanosilver pastes. Preparation of nanosilver particles and pastes, mechanisms of nanopastes sintering, and different rapid sintering processes are discussed. Emphasis is placed on the properties of sintered joints obtained by different sintering processes such as electric current assisted sintering, spark plasma sintering, and laser sintering, etc. Although the research on rapid sintering processes for nanosilver pastes has made a great breakthrough over the past few decades, investigations on mechanisms of rapid sintering, and the performance of joints fabricated by pastes with different compositions and morphologies are still far from enough.

Electrically conductive adhesives (ECAs) are one of the low temperature bonding materials. It can be used to replace toxic Sn-Pb solder. The key issue for the application of ECAs is how to improve their electrical properties. In the present study, we develop an effective method to promote the electrical properties of ECAs by addition of polyaniline (PANI) nanoparticles. PANIs were synthesized via a facile one-step chemical oxidative polymerization method. After adding 0.5 wt% PANI nanoparticles, the conductivity of ECAs increased dramatically by an order of magnitude. The bulk resistivity of 8.8 × 10⁻⁵ Ω·cm is achieved for 65 wt% silver fillers with 0.5 wt% PANIs loaded ECAs. Besides, this improvement has no negative effect on the shear strength and the aging life of ECAs. Moreover, the use of PANIs not only lowers the percolation threshold of ECAs, but also reduces the cost and improves the bonding reliability. Finally, PANIs enhanced ECAs patterns were successfully printed by a stencil printing method, which proved their potential applications in replacing conventional solder pastes and printing functional circuits.

By using pulse electrodeposition, a copper nanopillar array (CuNPA) was filled into porous anodized aluminum oxide (AAO) films to achieve a highly thermal conductive interconnector with anisotropic property. After 120 min pulse deposition, CuNPA uniformly filled the pores of AAO with a pore-filling percentage of 99.4%, as the ion concentration in AAO pores can re-equilibrate to electrolyte concentration during the current-off period. The CuNPA-filled AAO film showed a high thermal conductivity of 153.12 W/(m·K) in the vertical direction and a low thermal conductivity of 3.43 W/(m·K) in the horizontal direction. Hence, the anisotropic ratio of the thermal conductivity reached 44.64. Moreover, the fabrication process was facile and cost-effective, showing a potential application prospect in the field of high-density packages and power electronic devices.