Cracks and delamination, resulting from residual stresses, are a barrier in the world of additive manufacturing and selective laser melting (SLM) that prohibits the use of many metals in this field. By preheating the baseplate, thermal gradients are lowered and stresses can be reduced. In this work, some initial tests were performed with M2 high speed steel (HSS). The influence of preheating on density and mechanical and physical properties is investigated. The paper shows many promising results for the production of SLM parts in materials that are very sensitive to crack formation and delamination. When using a preheating of 200 °C, crack-free M2 HSS parts were produced with a relative density of 99.8%.

Due to unique functional and mechanical properties, NiTi shape memory alloys are one of the most promising metallic functional materials. However, the poor workability limits the extensive utilization of NiTi alloys as components of complex shapes. The emerging additive manufacturing techniques provide high degrees of freedom to fabricate complex structures. A freeform fabrication of complex structures by additive manufacturing combined with the unique functional properties (e.g., shape memory effect and superelasticity) provide great potential for material and structure design, and thus should lead to numerous applications. In this review, the unique microstructure that is generated by selective laser melting (SLM) is discussed first. Afterwards, the previously reported transformation behavior and mechanical properties of NiTi alloys produced under various SLM conditions are summarized.

The addition of 0.1 wt % carbon nanoparticles significantly improved the optical absorption and flowability of gas-atomized copper powder. This facilitated selective laser melting (SLM) by reducing the required laser energy density to obtain 98% dense parts. Moreover, the carbon addition led to an in situ de-oxidation of the copper parts during the SLM process. The properties of the as-built copper parts were limited to a tensile strength of 125 MPa, a ductility of 3%, and an electrical conductivity of 22.7 × 10⁶ S/m, despite the advantageous effect of carbon on the powder characteristics and SLM behavior. The modest mechanical properties were associated with the segregation of carbon nanoparticles and other impurities, such as phosphorus and oxygen along grain boundaries of epitaxially grown grains. Whereas, the low electrical conductivity was mainly attributed to the phosphorus impurity in solid-solution with copper.

Oil & Gas Science and Technology - Revue d'IFP Energies nouvelles

Besides the unique shape memory effect and superelasticity, NiTi alloys also show excellent damping properties. However, the high damping effect is highly temperature-dependent, and only exists during cooling or heating over the temperature range where martensitic transformation occurs. As a result, expanding the temperature range of martensite transformation is an effective approach to widen the working temperature window with high damping performance. In this work, layer-structured functionally graded NiTi alloys were produced by laser powder bed fusion (L-PBF) alternating two or three sets of process parameters. The transformation behavior shows that austenite transforms gradually into martensite over a wide temperature range during cooling, and multiple transformation peaks are observed. A microstructure composed of alternating layers of B2/B19′ phases is obtained at room temperature. The functionally graded sample shows high damping performance over a wide temperature range of up to 70 K, which originates from the gradual formation of the martensite phase during cooling. This work proves the potential of L-PBF to create NiTi alloys with high damping properties over a wide temperature range for damping applications.