Polypyrrole nanotubes exhibit conductivity of tens S cm⁻¹ which is one of the highest among the current conducting polymers.

Conducting polymers (CP), namely polyaniline (PANI) and polypyrrole (PPy), are promising materials applicable for the use as biointerfaces as they intrinsically combine electronic and ionic conductivity. Although a number of works have employed PANI or PPy in the preparation of copolymers, composites, and blends with other polymers, there is no systematic study dealing with the comparison of their fundamental biological properties. The present study, therefore, compares the biocompatibility of PANI and PPy in terms of cytotoxicity (using NIH/3T3 fibroblasts and embryonic stem cells) and embryotoxicity (their impact on erythropoiesis and cardiomyogenesis within embryonic bodies). The novelty of the study lies not only in the fact that embryotoxicity is presented for the first time for both studied polymers, but also in the elimination of inter-laboratory variations within the testing, such variation making the comparison of previously published works difficult. The results clearly show that there is a bigger difference between the biocompatibility of the respective polymers in their salt and base forms than between PANI and PPy as such. PANI and PPy can, therefore, be similarly applied in biomedicine when solely their biological properties are considered. Impurity content detected by mass spectroscopy is presented. These results can change the generally accepted opinion of the scientific community on better biocompatibility of PPy in comparison with PANI.

This article presents a contribution to better understanding of the processes which take place during the synthesis of polypyrrole nanotubes using a structure-guiding agent, methyl orange. Polypyrrole was prepared by oxidation of pyrrole monomer with iron(III) chloride. In the presence of methyl orange, the formation of nanotubes was observed instead of the globular morphology. Two reaction schemes with reversed additions of oxidant and monomer have been tested and they show remarkable influence on the produced morphology. Nanotubes with circular or rectangular profiles and diameters from tens to hundreds of nanometres have been obtained. FTIR and Raman spectra were used to assess the molecular structure of polypyrrole and detect residual methyl orange in the samples. The conductivity of nanotubes compressed into pellets was as high as 68 S cm⁻¹. The mechanism of nanotubular formation starting at the nucleus produced with the participation of organic dye is proposed. The growth of a nanotube, however, proceeds in the absence of a template. An alternative mechanism for the formation of nanotubes, the coating of solid templates with a polypyrrole overlayer, is also discussed.