Turning wood into honeycombs: Wood is an attractive material for structural applications, but it usually works best as boards or sheets. Xiao et al . have developed a process for engineering hardwood that allows these sheets to be manipulated into complex structures (see the Perspective by Tajvidi and Gardner). The key is to manipulate the cell wall structure by shrinking and blasting open the fibers and vessels by drying and “water-shocking” them. This process creates a window wherein the wood can be manipulated without ripping or tearing. Honeycomb, corrugated, or other complex structures are locked in once the wood dries. —BG

Six-times more carbon dioxide (CO ₂ ) is removed each year by terrestrial photosynthesis than fossil fuel emissions. However, the carbon is mostly returned to the atmosphere by decomposition. We found a 3775-year-old ancient wood log buried 2 meters belowground that was preserved far beyond its expected lifetime. The wood had near-perfect preservation, with carbon loss less than 5% compared to a modern sample. The lack of decay is likely due to the low permeability of the compact clay soil at the burial site. Our observation suggests a hybrid nature-engineering approach for carbon removal by burying woody biomass in similar anoxic environments. We estimate a global sequestration potential of up to 10 gigatonnes CO ₂ per year with existing technology at a low cost of $30 to $100 per tonne after optimization.

Natural cellulose-based materials (CBMs) have considerable potential as strong and lightweight materials for advanced structural applications. Herein, we demonstrate a mechanically strong yet lightweight CBM with highly aligned wood fibers by the coupling pulping of wood blocks with mechanical pressing, which exhibits a tensile strength of 719.0 ± 30.2 MPa, an elastic modulus of 19.0 ± 1.4 GPa, and a density of 1.32 g/cm³. The extraordinary mechanical properties of the CBM are mainly ascribed to the good orientation of wood fibers in the longitudinal direction as well as the dramatically increased hydrogen bonds among adjacent fiber cells due to the lignin removal and mechanical pressing. More significantly, the resulting sheet-like anisotropic CBMs can be used to fabricate anisotropic and isotropic bulk CBMs with maximum tensile strengths of 561 and 330 MPa, respectively, through a facile and scalable layer-by-layer stacking method. This work exploits the mechanical potential of cellulose and the large-scale production of anisotropic and isotropic bulk CBMs with extraordinary mechanical performance and may open up a range of novel applications to CBMs.