We have reported a new reduced graphene oxide–bismuth oxide composite that can be used as a supercapacitor electrode. Bi₂O₃ was synthesized from bismuth nitrate pentahydrate and oxalic acid as a precipitating agent using a hydrothermal process in an aqueous graphene oxide suspension. Instead of mixing graphene oxide with bismuth oxide, we have developed a bismuth oxalate precipitation between the layers. As prepared, composite of hydrated bismuth oxalate and graphene oxide was converted to bismuth oxide and reduced graphene oxide by thermal decomposition in a muffle stove. The material exhibited the specific capacitance of 94 F/g at current density 0.2 A/g. Using the cyclic voltammetry, the specific capacitance was as high as 55 F/g at scan rate 5 mV/s over the potential range 0–1 V. The material exhibited long-term cycle stability retaining 90 % specific capacitance after 3,000 cycles. Except Bi³⁺ ions present in Bi₂O₃, some amount of higher energy Bi⁵⁺ was confirmed.

Leaching of the dross containing 28.7% Sn, 18.0 Pb, 10.6% Cu, 8.9% Ge, 8.1% Zn, and 2.7% In in sulphuric and oxalic acid solution was investigated. The dross was obtained from thermal oxidation of by-product alloy generated during a New Jersey (NJ) zinc rectification process. The influence of different process conditions (temperature, time, acid concentration, and solid to liquid ratio) on leaching yield of the main components was determined. Additionally, the impact of oxidant (hydrogen peroxide, sodium hypochlorite, manganese (IV) oxide) addition on leachabilities was investigated. Germanium leaching yields exceeding 80% were observed for both sulphuric and oxalic acid solutions. Indium leachability in H₂C₂O_4(aq) was found at the level of 20%, while in H₂SO_4(aq), it strongly depends on process temperature, and reached 80% at 80 °C.

The precipitation of tannin complex of germanium from sulfuric solutions obtained after dross leaching was investigated. The tested solutions contained mainly zinc, germanium, indium, and tin. The influence of temperature, time, amount of added tannic acid and its purity was determined. The application of pure tannic acid allowed the precipitation of >99% of germanium and decreased its concentration in a solution 99% Sn and reduced its concentration in the solution below 0.025 g/dm³.

Antimony species was chemically anchored on graphene oxide using antimony (III) chloride precursor and then converted to the reduced graphene oxide-antimony species composite by a well-established polyol method. The resultant composite was successfully used as supercapacitor electrodes in a two-electrode symmetric system with aqueous electrolyte. The specific capacitance calculated from the galvanostatic charge/discharge curves obtained for this composite was 289 F/g. The enhanced capacitance results were confirmed by the electrochemical impedance spectroscopy and cyclic voltammetry. The high capacitance of the reduced graphene oxide-antimony species composite arises from the combination of double-layer charging and pseudocapacitance caused by the Faradaic reactions of the intercalated antimony species and residual surface-bonded functional groups.

Cementation of germanium from sulphate solution obtained after the leaching of GeIn dross using zinc dust was investigated. The composition of the examined solution was 5.15 Ge, 1.52 In, and 5.81 g/dm³ Zn. In order to resemble the solution before detinning, Sn concentration between 2–10 g/dm³ was also investigated. It was found that >99% of germanium may be precipitated from the solution. In order to achieve high selectivity, a detinned solution should be used because the precipitation yields of germanium and tin from the solution containing Sn were similar. For cementation with Zn powder at 75 °C for 2 h with a final pH of 2.0, over 99% of the germanium was removed from the solution, while the indium precipitation yield was 12%. The obtained cementate contained 50% Ge, mainly in elementary form.

Rhenium is an element that exhibits a broad range of oxidation states. Synthesis paths of selected rhenium compounds in its seventh oxidation state, which are common precursors for organic reaction catalysts, were presented in this paper. Production technologies for copper perrhenate, aluminum perrhenate as well as the ammonia complex of cobalt perrhenate, are thoroughly described. An ion exchange method, based on Al or Cu metal ion sorption and subsequent elution by aqueous perrhenic acid solutions, was used to obtain perrhenates. The produced solutions were neutralized to afford the targeted aluminum perrhenate and copper perrhenate products in high purity. The developed technologies allow one to manage the wastes from the production of these perrhenates as most streams were recycled. Hexaamminecobalt(III) perrhenate was produced by a newly developed method enabling us to produce a high purity compound in a reaction of spent hexaamminecobalt(III) chloride solution with a perrhenic acid. All prepared compounds are the basis for precursor preparation in organic catalysis.