The precipitation of tannin complex of germanium from sulfuric solutions obtained after dross leaching was investigated. The tested solutions contained mainly zinc, germanium, indium, and tin. The influence of temperature, time, amount of added tannic acid and its purity was determined. The application of pure tannic acid allowed the precipitation of >99% of germanium and decreased its concentration in a solution 99% Sn and reduced its concentration in the solution below 0.025 g/dm³.

The electronic components mounted on the printed circuit boards (PCBs) of mobile phones represent a resource that is rich in metals, and after separation from the boards, these components could be considered secondary raw materials. The concentrations of the valuable metals are insignificant when compared with those of complete PCBs; however, they could be significantly higher in a fraction formed from the separated components. This study focused on the analysis of Ag, Au, Cu, Nd, Nb, Ni, Pb, Pd, Sn, and Ta in fractions produced by the separation of all the components mounted on PCBs from several types of mobile phones. Atomic absorption spectrometry, atomic emission spectrometry, and mass spectrometry techniques were utilized, and a comparison of five older models of “brick” phones and five modern smartphones was conducted. Additionally, 50 kg of PCBs from the current recycling market were analyzed in the same way to create a summary of the current recycling stream.

Cementation of germanium from sulphate solution obtained after the leaching of GeIn dross using zinc dust was investigated. The composition of the examined solution was 5.15 Ge, 1.52 In, and 5.81 g/dm³ Zn. In order to resemble the solution before detinning, Sn concentration between 2–10 g/dm³ was also investigated. It was found that >99% of germanium may be precipitated from the solution. In order to achieve high selectivity, a detinned solution should be used because the precipitation yields of germanium and tin from the solution containing Sn were similar. For cementation with Zn powder at 75 °C for 2 h with a final pH of 2.0, over 99% of the germanium was removed from the solution, while the indium precipitation yield was 12%. The obtained cementate contained 50% Ge, mainly in elementary form.