Porous binary Ti-10Mo alloys were prepared using non-spherical titanium, molybdenum powders by the powder metallurgy (PM) space holder technique. Based on the three-dimensional analysis of porosity characteristics, a detailed assessment of the effects of porosity on mechanical properties and corrosion resistances in phosphate-buffered saline (PBS) was carried out. For comparison, PM-fabricated CP-Ti with 50.5% porosity sintered at 1200 °C for 2 h and dense Ti-10Mo alloy sintered at 1450 °C for 2 h (relative density is 97.2% and porosity is 2.8%) were studied simultaneously. The results show that with the space-holder volume contents rising from 63 to 79%, the open porosity and average pore size (d₅₀) increase remarkably, while the pore size distribution (d₁₀–d₉₀) tends to be stable at about 100 μm. The average pore sizes (d₅₀) of porous Ti-10Mo alloy can be controlled in the range of 70–380 μm. The PM-fabricated porous Ti-10Mo alloy can achieve a wide range of mechanical properties, with yield compression strength of 248.2–76.9 MPa, and elastic modulus of 6.4–1.7 GPa. In addition, the yield compression strength and the elastic modulus meet the linear regression and exponential formula, respectively. With the porosity of Ti-10Mo alloy increasing from 2.8 to 66.9%, the corrosion rate rises exponentially from 1.6 g/m²·day to 17.1 g/m²·day. In comparison to CP Ti with nearly the same porosity, Ti-10Mo alloy shows significantly higher corrosion resistance. As a result, the relationships between porosity and mechanical properties, corrosion resistances of Ti-10Mo alloys were established, which can be used as a design reference in material selection for orthopedic applications.

In this study, X-ray computed tomography was used to analyze powder binder separation in TC4 green bodies. Firstly, for the scanned results of the whole green body, because of the relative low resolution (36 µm), the powder binder separation can only be analyzed by using gray value distribution. Then, local regions (areas near the gate and the central parts) were scanned by using a much higher resolution (2.3 µm). Both of the volume fraction of powder content and gray value distributions indicate that powder particles tend to accumulate in the central parts. Finally, based on the results tested by using submicron resolution (0.8 µm), the effects of the volume and morphology of the powder particles on the powder binder separation were analyzed.

In Phase-Contrast Computed Tomography (PCCT), ring artifacts caused by inhomogeneity in the detector response manifest as vertical stripes in the sinogram and are accompanied by additional noise, degrading image quality and affecting subsequent analysis. This study proposes a novel method combining the least mean squares (LMS) algorithm with an alternating direction method of multipliers (ADMM)-based optimization model (ADOM). While ADOM effectively removes striping noise while preserving image details, its performance is limited in high-noise conditions. LMS algorithm preprocessing enhances ADOM model’s stability. Experimental results demonstrate that this method effectively eliminates ring artifacts and improves image quality.