Polyimide (PI) composite films with thicknesses of approximately 100 µm were prepared via a sol–gel reaction of 3-aminopropyltrimethoxysilane (APTMS) with poly(amic acid) (PAA) composite solutions using a thermal imidization process. PAA was synthesized by a conventional condensation reaction of two diamines, 3,5-diaminobenzoic acid (DABA), which has a carboxylic acid side group, and 2,2′-bis(trifluoromethyl)benzidine (TFMB), with 4,4′-(hexafluoroisopropylidene)diphthalic anhydride (6FDA) in N,N-dimethylacetamide (DMAc). The PAA–silica composite solutions were prepared by mixing PAA with carboxylic acid side groups and various amounts of APTMS in a sol–gel process in DMAc using hydrochloric acid as a catalyst. The obtained PI–silica composite films showed relatively good thermal stability, and the thermal stability increased with increasing APTMS content. The optical properties and in-plane coefficient of thermal expansion (CTE) values of the PI–silica composite films were investigated. The CTE of the PI–silica composite films changed from 52.0 to 42.1 ppm/°C as the initial content of APTMS varied. The haze values and yellowness indices of the composite films increased as a function of the APTMS content.

In this exploratory study, we searched for associations between the two most common diseases of the oral cavity—dental caries and periodontal diseases—taking into account additional factors, such as personalized clinical pictures (the individual risk factors of the patient), based on the method of a multivariate data analysis of the molecular changes in the composition of human gingival crevicular fluid (GCF). For this purpose, a set of synchrotron Fourier-transform infrared spectroscopy (FTIR) spectra of gingival crevicular fluid samples from patients with different demographics, levels of dental caries development and periodontal diseases, and the presence/absence of concomitant chronic diseases were obtained and analyzed. Using a set of techniques (v-, F-, Chi-square tests; a principal component analysis (PCA); and the hierarchical clustering of principal components (HCPCs)) implemented in the R package FactoMineR allowed us to assess the relationship between the principal components (PCs) and characteristics of the respondents. By identifying the features (vibrational modes in the FTIR spectra) that contribute most to the differentiation of the spectral dataset, and by taking into account the interrelationships between the patients’ characteristics, we were able to match specific biological markers (specific molecular groups) to the two factors of interest—two types of oral pathologies. The results obtained show that the observed changes in the quantitative and qualitative composition of the modes in the infrared (IR) spectra of the GCF samples from patients with different dental caries developments and periodontal diseases present confirm the difficulty of identifying patient-specific spectral information. At the same time, different periodontal pathologies are more closely associated with other characteristics of the patients than the level of their caries development. The multivariate analysis performed on the spectral dataset indicates the need to take into account not only the co-occurrence of oral diseases, but also some other factors. The lack of this consideration (typical in lots of studies in this area) may lead to misinterpretations and consequently to a loss of data when searching for biological markers of certain oral diseases.

Biodegradable poly-[(R)-3-hydroxybutyrate-co-(R)-3-hydroxyhexanoates] (PHBHx) have been widely studied for their applications in potentially replacing petroleum-based thermoplastics. In this study, the effect of the high molecular weight (Mn = 3400) poly(ethylene glycol) (PEG) blended in the films of PHBHx with different ratios of PEG was investigated using chemical FTIR imaging. Chemical IR images and FTIR spectra measured with increasing temperature revealed that PEG plays an important role in changing the kinetics of PHBHx crystallization. In addition, two-dimensional correlation spectra clearly showed that thermal properties of PHBHx/PEG blend film changed when the blending ratio of PHBHx/PEG were 60/40 and 50/50. Consequently, PEG leads to changes in the thermal behavior of PHBHx copolymers.