Effective thermal conduction modification in asphalt binders is beneficial to reducing pavement surface temperature and relieving the urban heat island (UHI) effect in the utilization of solar harvesting and snow melting pavements. This study investigated the performance of two nanometer-sized modifiers, graphene (Gr) and carbon nanotubes (CNTs), on enhancing the thermal, physical and rheological properties of asphalt binders. Measurements depending on a transient plant source method proved that both Gr and CNTs linearly increased the thermal conductivity and thermal diffusivity of asphalt binders, and while 5% Gr by volume of matrix asphalt contributed to 300% increments, 5% CNTs increased the two parameters of asphalt binders by nearly 72% at 20 °C. Meanwhile, a series of empirical and rheological properties experiments were conducted. The results demonstrated the temperature susceptibility reduction and high-temperature properties promotion of asphalt binders by adding Gr or CNTs. The variation trends in the anti-cracking properties of asphalt binders modified by Gr and CNTs with the modifier content differed at low temperatures, which may be due to the unique nature of Gr. In conclusion, Gr, whose optimal content is 3% by volume of matrix asphalt, provides superior application potential for solar harvesting and snow melting pavements in comparison to CNTs due to its comprehensive contributions to thermal properties, construction feasibility, high-temperature performance and low-temperature performance of asphalt binders.

Styrene–butadiene copolymer (SBS)-modified bitumen (SMB) is widely applied in pavement construction. With yearly services, many SMB wastes urgently need to be reclaimed for repaving roads based on the objectives of environmental protection, landfill saving, as well as resource utilization. The present work is focused on the investigation of the physical and rheological properties of aged SMB incorporated with rejuvenating systems consisting of fluid catalytic cracking slurry (FCC slurry), C12–14 aliphatic glycidyl ether (AGE), diphenylmethane diisocyanate (MDI), and other additives. The rejuvenating systems containing the main components of 10% FCC slurry, 10%FCC/3%AGE, and 10%FCC/3%AGE/1% MDI were respectively recorded as R_a, R_b, and R_c. The results indicate that both R_b and R_c have obvious workability that make contributions for improving comprehensive physical properties while slightly reducing the softening point, which were also proven to be effective for the re-rejuvenation of re-aged binder. The higher viscous-elastic temperature caused by the agglomeration of binder molecules in aged SMB could be dropped to a lower value with rejuvenating systems, while improving the low-temperature crack resistance. With the use of the R_b and R_c rejuvenating systems, the high-temperature deformation resistance of aged SMB fell, approaching the performance of fresh SMB. Vibration noise consumption could be improved for aged SMB incorporated with R_b and R_c in the form of viscous loss, while the effects for re-aged SMB containing the same rejuvenating systems were weakened but still effective.