A highly sensitive glucose sensor was prepared by a one-step method using 3-aminophenyl boronic acid as a unit of recognition and a screen-printed carbon electrode (SPCE) as an electrochemical transducer. Scanning Electron Microscopy confirmed the success of the functionalization of the SPCE due to the presence of clusters of boronic acid distributed on the carbon surface. In agreement with the Electrochemical Impedance Spectroscopy (EIS) tests performed before and after the functionalization, Cyclic Voltammetry results indicated that the electroactivity of the electrode decreased 37.9% owing to the presence of the poly phenylboronic acid on the electrode surface. EIS revealed that the sensor was capable to selectively detect glucose at a broad range of concentrations (limit of detection of 8.53 × 10⁻⁹ M), not recognizing fructose and sucrose. The device presented a stable impedimetric response when immediately prepared but suffered the influence of the storage time and some interfering species (dopamine, NaCl and animal serum). The response time at optimized conditions was estimated to be equal to 4.0 ± 0.6 s.

A new non-invasive and flexible sensor was fabricated to monitor the muscular activity of upper body muscles. It consists of a dry electrode made of multimaterial metal-polymerglass hollow-core fiber electrodes connected to a custom made signal acquisition platform. This fiber electrode only adds a negligible contribution to the recording systems internal noise (7.626 μV peak-to-peak and 1.234 μV RMS; recording system noise: 6.901 μV peak-to-peak and 1.205 μV RMS). Surface electromyograms (sEMGs) of the biceps bracci and trapezius muscles were recorded during maximal voluntary contractions using the new sensor and compared to that obtained with medical grade commercial sensors. Frequency content and time domain analysis show that the new flexible sensor performs similarly to commercial devices in terms of sEMG signal amplitude discrimination and frequency shift evaluation during the development of muscle fatigue. The advantage of the new sensor is the high flexibility of the fibers allowing their easy integration into stretchable garments without compromising the user’s comfort. This will lead to the development of a new generation of smart textile with large application for telemedicine and assistive devices.

Screen-printed carbon electrode (SPCE) was examined as a transducer substrate for application in electrochemical sensors. Aqueous solutions of 0.1 M KCl and 0.1 M KCl + 5 mM K3[Fe(CN)6]/K4[Fe(CN)6] (redox solution) were prepared to simulate the environment of faradaic and non-faradaic sensing, respectively. The SPCE presented an irregular surface composed by two main carbon phases. Raman spectroscopy results revealed the presence of peaks around 1,580 cm−1 and 1,334 cm−1 related to the G and D bands corresponding to sp2 carbon atoms (graphite flakes) and a multitude of broad bands associable to amorphous sp3 carbon in the ink matrix. Conductive atomic force microscopy indicated that the irregular structure of the SPCE led to the heterogeneous distribution of the current over the surface and the electroactivity of this material was mainly attributed to the presence of graphite. Polarization curves and electrochemical impedance spectroscopy (EIS) revealed that the redox solution was more aggressive to the SPCE, despite this electrode was achieved a quasi-steady state for 1 h under the effect of a polarization potential in both electrolytes, which justifies its use as an electrochemical transducer in faradaic and non-faradaic devices.