The biopolymer solid electrolyte has been synthesized and characterized. Potassium iodide (KI) has been added in polymer matrix to develop solid polymer electrolyte. Relationships between electrical, ionic transport parameter and mechanism have been studied in detail. Impedance spectroscopy reveals the detailed electrical studies and ion transport mechanism. The ion dissociation factor is compared with a measured dielectric constant at a fixed frequency. The dielectric data are calculated which support the ionic conductivity data.

A new generation of boronic ionic liquid namely 1-ethyl-3-methylimidazolium difluoro(oxalate)borate (EMImDFOB) was synthesized by metathesis reaction between 1-ethyl-3-methylimiazolium bromide and lithium difluoro(oxalate)borate (LiDFOB). Ternary gel polymer electrolyte membranes were prepared using electrolyte mixture EMImDFOB/LiDFOB with poly vinylidenefluoride-co-hexafluoropropylene (PVdF-co-HFP) as a host matrix by facile solvent-casting method and plausibly demonstrated its feasibility to use in lithium ion batteries. Amongst ternary gel electrolyte membrane, DFOB-GPE3, which contained 80 wt% of EMImDFOB/LiDFOB and 20 wt% PVdF-co-HFP, showed excellent electrochemical and cycling behaviors. The highest ionic conductivity was found to be 10⁻³ Scm⁻¹ at 378 K. Charge-discharge profile of Li/DFOB-GPE3/LiCoO₂ coin cell displayed a maximum discharge capacity of 148.4 mAhg⁻¹ at C/10 rate with impressive capacity retention capability and columbic efficiency at 298 K.