Ice accretion on external aircraft surfaces due to the impact of supercooled water droplets can negatively affect the aerodynamic performance and reduce the operational capability and, therefore, must be prevented. Icephobic coatings capable of reducing the adhesion strength of ice to a surface represent a promising technology to support thermal or mechanical ice protection systems. Icephobicity is similar to hydrophobicity in several aspects and superhydrophobic surfaces embody a straightforward solution to the ice adhesion problem. Short/ultrashort pulsed laser surface treatments are proposed as a viable technology to generate superhydrophobic properties on metallic surfaces. However, it has not yet been verified whether such surfaces are generally icephobic under representative icing conditions. This study investigates the ice adhesion strength on Ti6Al4V, an alloy commonly used for aerospace components, textured by means of direct laser writing, direct laser interference patterning, and laser‐induced periodic surface structures laser sources with pulse durations ranging from nano‐ to femtosecond regimes. A clear relation between the spatial period, the surface microstructure depth, and the ice adhesion strength under different icing conditions is investigated. From these observations, a set of design rules can be defined for superhydrophobic surfaces that are icephobic, too.

Forward facing aerodynamic surfaces such as rotors and wings are susceptible to ice build‐up when exposed to atmospheric icing conditions. If not removed, accumulated ice on aircraft surfaces affects aerodynamics or rotation balance, which can ultimately lead to increased fuel consumption, reduced operational performance and to potentially hazardous situations. Laser surface structuring is proposed as an alternative technology to coatings for achieving icephobic properties and support anti‐icing and de‐icing processes on aerodynamic surfaces. However, to authors’ knowledge, no study available in the literature reports on the icing behavior of microtextured curved aerodynamic profiles and the effect of the laser surface treatment on the electrothermal heating used for ice protection systems. In this work, direct laser interference patterning is employed to fabricate hierarchical micro‐ and nanostructures directly on a non‐planar titanium airfoil. The anti‐icing performance of the laser‐treated airfoil is tested in an icing wind tunnel under simulated atmospheric conditions. The results demonstrate a self‐limiting ice growth, a decrease in the deicing electro‐thermal power up to 80%, and up 60% lower heating power necessary to keep the surface free of ice than on the reference airfoil.

Controlling laser induced surface morphology is essential for developing specialized functional surfaces. This work presents novel, multi-scale periodic patterns with two-dimensional symmetry generated on stainless steel, polyimide and sapphire. The microstructures were realized by combining Direct Laser Interference Patterning with the generation of Laser Induced Periodic Surface Structures in a one-step process. An industrial, fiber femtosecond laser source emitting at 1030 nm with a pulse duration of 500 fs was utilized for the experiments. In the case of stainless steel, it was possible to create line-like or pillar-like surface patterns by rotating the polarization orientation with respect to the interference pattern. In the case of polyimide and sapphire, the absorption of the laser radiation was promoted by a multiphoton mechanism. In polyimide, grooves and pillars of several microns in depth were produced over an area much larger than the spot size. Finally, for sapphire, the simultaneous generation of interference-like pattern and laser induced periodic surface structures was realized. The results reported here provide valuable data on the feasibility to combine two state-of-the-art techniques with an industrial apparatus, to control the induced surface morphology.

In this work, hierarchical surface patterns fabricated on Ti-6Al-4V alloy combining two laser micro-machining techniques are presented. The used technologies are based on nanosecond Direct Laser Writing and picosecond Direct Laser Interference Patterning. Squared shape micro-cells with different hatch distances were produced by Direct Laser Writing with depths values in the micro-scale, forming a well-defined closed packet. Subsequently, cross-like periodic patterns were fabricated by means of Direct Laser Interference Patterning using a two-beam configuration, generating a dual-scale periodic surface structure in both micro- and nano-scale due to the formation of Laser-Induced Periodic Surface Structure after the picosecond process. As a result a triple hierarchical periodic surface structure was generated. The surface morphology of the irradiated area was characterized with scanning electron microscopy and confocal microscopy. Additionally, static contact angle measurements were made to analyze the wettability behavior of the structures, showing a hydrophobic behavior for the hierarchical structures