Metal oxide titanium dioxide (TiO₂) nanoparticles were synthesized by using a simple and economical sol-gel method. The prepared nanoparticles were used to evaluate methylene blue dye degradation and as catalysts in the oxidation of benzaldehyde. The crystallite size of the titanium dioxide nanoparticle was 18.3 nm, which was confirmed by X-ray diffraction analysis. The spherical morphology was confirmed by scanning electron microscopy (SEM), and the elemental composition of the nanoparticle was found by energy dispersive X-ray (EDAX) analysis. The anatase form of the nanoparticle was confirmed by the bandgap 3.2 eV, which was measured using UV–DRS analysis. The bond between metal and oxygen was confirmed by the peaks at 485 and 606 cm^–1 analyzed by Fourier transform infrared analysis (FTIR). The efficiency of the catalyst in dye degradation was 60.08, 68.38, and 80.89% with respect to 50, 75, and 100 mg catalyst weight. The yield % of benzoic acid was 94%, and the reduction efficiency against 4-nitrophenol was 98.44%.

${\text{BaSnF}}_4$ fluoride ion conductor has been prepared by mechanochemical milling technique at room temperature. The as-prepared material crystallizes in the cubic fluorite-type structure due to disordering of metal cations. The cubic phase transforms to tetragonal structure by annealing at 460 K. The ionic conductivity of the cubic phase is two to three orders of magnitude lower than the annealed sample. The complex conductivity of the investigated materials has been analyzed by a power-law model in order to extract the hopping rates and the concentration of mobile ions, the parameters that control the overall conduction behavior. The estimated values of the concentration of mobile ions are found to be of the same order, indicating that the conduction process is controlled by the mobility of charge carriers. ${\text{BaSnF}}_4$ has been found to belong to a new class of nonoxidic giant dielectric constant materials with a value of ${\epsilon }^{\prime }\sim {10}^5$ , which is independent of temperature and frequency over wide ranges. It is found that the giant values of the dielectric constant are not due to surface barrier layer capacitance effects at the sample/electrode interface of the material.

The preparation, characterization, and application of Nickel oxide (NiO)–Copper oxide (CuO)–Zinc oxide (ZnO) transition nanometal oxides have significantly enhanced their tunable properties for superior multifunctional performances compared with well-known metal oxides. NiO–CuO–ZnO nano transition metal oxides were synthesized by a simple eco-friendly solution combustion method. X-ray diffraction studies revealed distinct phases such as monoclinic, cubic, and hexagonal wurtzite for CuO, NiO, and ZnO, respectively, with NiO having the highest composition. The particle sizes were found to be in the range between 25 and 60 nm, as determined by powder X-ray diffraction. The energy bandgap values were found to be 1.63, 3.4, and 4.2 eV for CuO, ZnO, and NiO, respectively. All metal oxides exhibited a moderate degradation efficiency for AR88 dye. The results of ultraviolet–visible absorption spectra helped identify the bandgap of metal oxides and a suitable wavelength for photocatalytic irradiation. Finally, we concluded that the electrochemical studies revealed that the synthesized materials are well suitable for sensor applications.

This article outlines the preparation of manganese-doped copper nanoparticles (Mn + Cu NPs) using Vinca rosea (L.) leaf extract as a convenient and environmentally friendly substance. UV–vis, FT–IR, XRD, SEM–EDAX, and DLS instrumental techniques were employed to describe the physical and chemical properties of synthesized V. rosea extract-mediated Vr-Mn + Cu NPs. The synthesized Vr-Mn + Cu NPs were observed to be monodispersed and spherical, with an average size of 412 nm. The plant extract includes a variety of phytochemical components. The Vr-Mn + Cu NPs also have potential antioxidant and antibacterial properties against selected pathogens. The green synthesized Vr-Mn + Cu NPs showed a maximum inhibition zone of 16.33 ± 0.57 mm against E. coli. For dye degradation, MR, EBT, and MO showed the highest degradation percentage capabilities with Vr-Mn + Cu NP-based adsorbents, which were determined to be 78.54 ± 0.16, 87.67 ± 0.06, and 69.79 ± 0.36. The results clearly show that biosynthesized Vr-Mn + Cu NPs may be employed as an antioxidant, antibacterial, photocatalytic dye degradation, and catalytic agent, as well as being ecologically benign.

Nanoceramics of CaCu₃Ti₄O₁₂ (CCTO) were synthesized by mechanosynthesis and spark plasma sintering with grain size of 150–200 nm. Giant dielectric constant properties are observed in the CCTO nanoceramics due to internal barrier layer capacitance (IBLC) effects. Impedance spectroscopy data suggest that the presence of resistive grain boundaries in addition to resistive domain boundaries is the origin of the IBLCs in CCTO nanoceramics.