Vanadium dioxide (VO₂) thermochromic thin films with various thicknesses were grown on quartz glass substrates by radio frequency (RF)-plasma assisted oxide molecular beam epitaxy (O-MBE). The crystal structure, morphology and chemical stoichiometry were investigated systemically by X-ray diffraction (XRD), atomic force microscopy (AFM), Raman spectroscopy and X-ray photoelectron spectroscopy (XPS) analyses. An excellent reversible metal-to-insulator transition (MIT) characteristics accompanied by an abrupt change in both electrical resistivity and optical infrared (IR) transmittance was observed from the optimized sample. Remarkably, the transition temperature (T_MIT) deduced from the resistivity-temperature curve was reasonably consistent with that obtained from the temperature-dependent IR transmittance. Based on Raman measurement and XPS analyses, the observations were interpreted in terms of residual stresses and chemical stoichiometry. This achievement will be of great benefit for practical application of VO₂-based smart windows.

A graphene coated hexagonal ZnO (HZO@Gr) with enhanced activity in photocatalysis was synthesized. However, the photoinduced charge transfer behavior and the beneficial role of graphene in promoting photocatalytic reactions have not been sufficiently investigated experimentally. In this paper, the surface potentials of the ±(0001)-polar plane of HZO (Zn-polar plane and O-polar plane), graphene, graphene/Zn-polar plane and graphene/O-polar plane were measured using Kelvin probe force microscopy (KPFM). On the basis of the KPFM results, the respective Fermi levels were calculated and the internal electric field (IEF) of HZO was confirmed. Taking the IEF of HZO into consideration, the three-dimensional band diagrams of the HZO@Gr composites in methyl blue (MB) solution in the dark and under UV-visible irradiation after equilibrium were proposed. Accordingly, it is found that there could emerge different interactions between graphene and HZO at the ±(0001)-polar plane of HZO. Furthermore, the photogenerated holes and electrons tend to migrate to opposite directions. With the participation of graphene and IEF, the composites show a decrease in possibility of charge recombination. As a result, the active groups, namely ˙OH and ˙O₂ ⁻ radicals, could be mainly generated at/near the O-polar plane and Zn-polar plane, respectively. This work can serve as a supplemental explanation of the charge transfer during the photocatalytic process at the polar ZnO/graphene composite surface.

Thermal control materials are employed to adjust the temperature of a spacecraft operating in deep space. The spectral emissivity is a crucial factor in evaluating the thermal radiative properties of such materials. An apparatus, composed of a Fourier transform infrared spectrometer (FTIR), a sample cooling chamber and a mechanical modulation system was demonstrated to measure low temperature infrared spectral emissivity under vacuum. The mechanical modulation system, which includes a chopper and a lock-in amplifier, is employed to reduce the interference of background radiation during measurements. The limitation of the Fourier transform frequency on the chopper frequency can be eliminated by setting the FTIR on step-scan mode. The apparatus is separated into two parts and evacuated by different pumps. In this study, a high quality emission spectrum of a sample is measured by the apparatus. The spectral emissivity of thermal control materials are obtained in the wavelength range of 8 to 14 μm at 173 and 213 K. The combined standard uncertainty of the apparatus is 3.30% at 213 K.

Pure, 5% Ti-doped and 10% Ti-doped WO₃ thin films were prepared by the radio frequency magnetron sputtering and characterised by a SEM, an electrochemical workstation and an UV–VIS–NIR spectrophotometer. Research results showed that Ti doping had no apparent influence on the surface morphology and optical band gap. It could also be found that the addition of Ti has little interference with the electrochromic property of WO₃ in both bleached and coloured states at initial cycles from electrochemical and optical test results, while there were apparent differences in the optical transmittance and inserted and extracted charge with increasing cycles. This is attributed that Ti-doped WO₃ thin films allow facile ion interaction/extraction and have less ion residues, which can stabilise the electrochemical cycling performance. Furthermore, the data we have obtained indicate that 5% Ti-doped WO₃ film has the best electrochromic property.