The thermal performance of wood–plastic composites (WPCs) with different fiber, different fiber contents, and different lubricants were investigated in this paper. The results show that the thermal degradation temperature, melting temperature, crystallization temperature, crystallinity, and viscosity of WPCs with wood fiber were slightly higher than those of WPCs with floor sanding powder and rice husk. As the wood fiber content increased, the melting temperature and crystallinity of WPCs decreased while the crystallization temperature, viscosity, and pseudoplasticity increased. When the wood fiber content was increased to 60%, the dimensional stability of WPCs tended to be constant, and a higher wood fiber content was not conducive for processing of WPCs. WPCs had a small coefficient of linear thermal expansion at low temperature and demonstrated a good dimensional stability. The presence of lubricant reduced the viscosity and increased the pseudoplasticity of the WPCs, which is advantageous for the dimensional stability of WPCs at low temperature while making it worse for high temperatures.

The advancement in science and technology has led to luffa sponge (LS) being widely used as a natural material in industrial application because of its polyporous structure and light texture. To enhance the utility of LS fibers as the reinforcement of lightweight composite materials, the current study investigates their water absorption, mechanical properties, anatomical characteristics and thermal performance. Hence, moisture regain and tensile properties of LS fiber bundles were measured in accordance with American Society for Testing and Materials (ASTM) standards while their structural characteristics were investigated via microscopic observation. Scanning electron microscopy (SEM) was used to observe the surface morphology and fractured surface of fiber bundles. The test results show that the special structure where the phloem tissues degenerate to cavities had a significant influence on the mechanical properties of LS fiber bundles. Additionally, the transverse sectional area occupied by fibers in a fiber bundle (S_F), wall thickness, ratio of wall to lumen of fiber cell, and crystallinity of cellulose had substantial impact on the mechanical properties of LS fiber bundles. Furthermore, the density of fiber bundles of LS ranged within 385.46–468.70 kg/m³, significantly less than that of jute (1360.40 kg/m³) and Arenga engleri (950.20 kg/m³). However, LS fiber bundles demonstrated superior specific modulus than Arenga engleri.

In this study, composites of poly (hydroxybutyrate-co-valerate) (PHBV) with untreated luffa fibers (ULF) and NaOH-H₂O₂ treated luffa fibers (TLF) were prepared by hot press forming. The properties of luffa fibers (LFs) and composites were characterized by scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR), and other analysis methods. Results showed that pre-treatment effectively removed pectin, hemicellulose, and lignin, thus reducing the moisture absorptivity of LFs. The flexural strength of TLF/PHBV was higher than that of ULF/PHBV. With 60% LF content, the flexural strengths of ULF/PHBV and TLF/PHBV reached 75.23 MPa and 90.73 MPa, respectively, 219.7% and 285.6% more than that of pure PHBV. Water absorptivities of composites increased with increase in LF content. Water absorptivity of TLF/PHBV was lower than that of ULF/PHBV. The flexural strengths of composites decreased after immersion in water at room temperature. Meanwhile, flexural strength of TLF/PHBV was lower than that of ULF/PHBV. Pretreatment of LFs effectively improved the bonding between fibers and PHBV, resulting in enhanced and thus improved the moisture resistance of composites.