Two years after the Zhanghewan Pumped-Storage Power Station was put into operation, more than 500 blisters appeared in the asphalt concrete facing of the upper reservoir, and nearly half of them ruptured at the surface. The blistering mechanism of the asphalt concrete facing was studied in this paper. Through on-site inspection and coring inspection, it was found that the blistering was caused by the vapor pressure formed by the water enclosed in the middle of the impervious layer during high temperatures. Numerical analysis showed that the temperature 5 cm below the surface could reach 50–60 °C. Through numerical analysis and model tests, the internal water at this temperature may form a vapor pressure of 20 kPa. Finally, the blister size of the asphalt concrete facing at this temperature and pressure was studied with a model test. The possible sources of moisture inside the impervious layer were also analyzed through a core test, which found that moisture was most likely to be introduced by water spraying during rolling.

The current methods for evaluating the contact condition between concrete and lining were the ground penetrating radar (GPR) and the coring method. The penetration of radar electromagnetic waves was greatly affected by steel reinforcement and water, which often made the detection results of GPR unsatisfactory. A spectral analysis of the surface wave (SASW) method was used to evaluate the concrete-bedrock interface condition for hydraulic tunnel linings in this paper, since the impact elastic wave is less affected by steel bars and water content. An SASW implementation program based on fast Fourier transformation (FFT) was developed to analyze data from numerical simulations and field tests. Various models were studied to investigate the feasibility of using numerical analysis. For the first time, the study was employed to find out the influences of different receiver spacings and impact duration on the efficiency of detecting the existence of a weak layer underneath the concrete using the SASW method. On this basis, in-situ tests were carried out to verify the applicability in the field and results were verified by coring. In the research, the following results were found: (1) The finite element analysis results of different uniform or layered models showed that the SASW method could accurately identify the interface contact condition between the concrete lining and bedrock, especially the existence of voids; (2) when the receiver spacing was 1.0–1.5 times the thickness of the target object to be inspected, the quality of the collected signal data was the best; (3) under a certain reasonable range, the impact duration had an insignificant effect on the phase spectra and dispersion curves of a concrete-weak layer model; (4) in-situ SASW inspection could accurately tell whether the voids exist at the concrete-bedrock interface; and (5) the data processing program of the SASW method based on the MATLAB platform was accurate, convenient, and worth promoting.

In this paper, we experiment on the hydraulic fracturing of asphalt concrete with a voids content higher than 3%, which has arisen from the possible local shear dilatancy of Quxue asphalt’s core wall of concrete core dam, the highest one of the sort constructed in the world. The model test has shown that under the sole water pressure 0.13 MPa—relevant to the pressure where the dilatancy could appear at core wall of Quxue dam—the asphalt concrete with a voids content of 3.5% underwent hydraulic fracturing. Furthermore, the asphalt concrete with a voids content of 3.0% was tested for nearly 500 h and no sign of hydraulic fracturing was found, which again confirmed the threshold requirement for a 3% voids content to the impervious asphalt concrete to the hydraulic fracture concern. According to the analysis of the test result, the theory of fracture mechanics could be applied to the hydraulic fracture of asphalt concrete with a voids content between 3.4~4.0%, which behaved during hydraulic fracturing like a quasi-brittle material, similar to concrete. Because the hydraulic fracturing could occur in the shear dilatant asphalt concrete, a proper mix proportion of asphalt concrete to a project with adverse stress state should be carefully designed to rule out the possibility of shear dilatancy.