Although the abrasive waterjet (AWJ) has been widely used for steel cutting for decades and there are hundreds of research papers or even books dealing with this technology, relatively little is known about the relation between the steel microstructure and the AWJ cutting efficiency. The steel microstructure can be significantly affected by heat treatment. Three different steel grades, carbon steel C45, micro-alloyed steel 37MnSi5 and low-alloy steel 30CrV9, were subjected to four different types of heat treatment: normalization annealing, soft annealing, quenching and quenching followed by tempering. Then, they were cut by an abrasive water jet, while identical cutting parameters were applied. The relations between the mechanical characteristics of heat-treated steels and the surface roughness parameters Ra, Rz and RSm were studied. A comparison of changes in the surface roughness parameters and Young modulus variation led to the conclusion that the modulus was not significantly responsible for the surface roughness. The changes of RSm did not prove any correlation to either the mechanical characteristics or the visible microstructure dimensions. The homogeneity of the steel microstructure appeared to be the most important factor for the cutting quality; the higher the difference in the hardness of the structural components in the inhomogeneous microstructure was, the higher were the roughness values. A more complex measurement and critical evaluation of the declination angle measurement compared to the surface roughness measurement are planned in future research.

Significant structural steels for nuclear power engineering are chromium-nickel austenitic stainless steels. The presented paper evaluates the kinetics of the fatigue crack growth of AISI 304L and AISI 316L stainless steels in air and in corrosive environments of 3.5% aqueous NaCl solution after the application of solution annealing, stabilizing annealing, and sensitization annealing. Comparisons were made between the fatigue crack growth rate after each heat treatment regime, and a comparison between the fatigue crack growth rate in both types of steels was made. For individual heat treatment regimes, the possibility of the development of intergranular corrosion was also considered. Evaluations resulted in very favourable corrosion fatigue characteristics of the 316L steel. After application of solution and stabilizing annealing at a comparable ∆K level, the fatigue crack growth rate was about one half compared to 304L steel. After sensitization annealing of 316L steel, compared to stabilizing annealing, the increase of crack growth rate during corrosion fatigue was slightly higher. The obtained results complement the existing standardized data on unconventional characteristics of 304L and 316L austenitic stainless steels.

A pulsating waterjet is a technological modification of a conventional waterjet that utilizes ultrasonic vibrations to generate a modulated jet, resulting in repetitive fatigue loading of the material. The erosion efficiency of the ultrasonic pulsating waterjet is majorly determined by the hydraulic factors and its interaction with standoff distance. However, the dependency of the wear rates on different hydraulic factors and formulation of an implicit prediction model for determining effective standoff distance is still not present to date. Therefore, in this study, the combined dependency of the supply pressure (20-40 MPa), nozzle diameter (0.3-1.0 mm), and standoff distance (1-121 mm) on wear rates of AW-6060 aluminum alloy are studied. Statistical analysis is used to determine the statistically significant factors and formulate regression equations to determine output responses within the experimental domain. The surface topography and sub-surface microhardness of the eroded grooves were studied. The results show that both the disintegration depth and the material removal increase with an increase in the nozzle diameter and supply pressure. However, the dependency of the output responses on nozzle diameter is statistically more evident than supply pressure and two-way interactions. Cross-sectional images of the grooves showed typical hydrodynamic erosion characteristics in erosion cavities, subsurface voids, and material upheaving. The results of microhardness analysis showed an approximately 15-20% increase in hardness values compared to the untreated samples.

More efficient ways to process materials are constantly being sought, even in the case of continuous water flow technology, which acts on materials mainly by stagnant pressure. An alternative method is an ultrasound-stimulated pulsating water jet, the basis of which is the repeated use of impact pressure, which reduces the time interval for mechanical relaxation. This article focuses on a comparative study from the point of view of water mass flow rate on material penetration and its integrity. Relatively low pressures (p = 20, 30, and 40 MPa) with varying nozzle diameters (d = 0.4 and 0.6 mm) were used to identify the effectiveness of the pulsating water jet. The time exposure of the jet at a fixed place was varied from t = 0.5 to 5 s for each experimental condition. The results showed that with an increase in the pressure and diameter values, the disintegration depth increased. In addition, the surface topography and morphology images showed signs of ductile erosion in the form of erosion pits, upheaved surfaces, and crater formation. The microhardness study showed an increase of 10% subsurface microhardness after the action of the pulsating water jet as compared to the original material.

Structures of carburized layers after the surface saturation process in gaseous, liquid or solid medium and after subsequent heat treatment (hardening and low-temperature tempering) consist mainly of high carbon plate martensite with a certain portion of retained austenite. The presence of retained austenite (RA) in carburized layers is mostly considered as undesirable because it decreases hardness of the hardened layer and furthermore, a spontaneous conversion to a ferritic-carbide mixture of a bainitic type, accompanied by a change of properties, dimensional instability and the local increase in internal stress with the possible formation of cracks, can occur. The proportion of retained austenite is, therefore, a significant characteristics of the quality of hardened layers. This work deals with the evaluation of the volume fraction of retained austenite in carburized layers using image analysis on metallographic images.

The use of low-carbon unalloyed steel with minimal silicon content is widespread in structural steel and automotive applications due to its ease of manipulation. The mechanical properties of this steel can be significantly enhanced through severe plastic deformation (SPD) techniques. Our study focuses on the practical benefits of the dual rolling equal channel extrusion (DRECE) method, which strengthens the steel and has implications for material hardness and the thickness of subsequently applied hot-dip zinc galvanizing. Furthermore, the steel’s corrosion potential and current are investigated as a function of material hardness and thickness. The findings show a 20% increase in hardness HV 30 after the first run through the forming machine, with an additional 10% increase after the second run. Subsequent galvanizing leads to a further 1–12% increase in HV 30 value. Notably, the DRECE hardening demonstrates no statistically significant effect on the corrosion potential and current; however, the impact of galvanizing is as anticipated.