In this study, a variety of industrial solid wastes, including petroleum coke desulfurization slag, fly ash and carbide slag with natural resource bauxite, were used as raw materials to prepare high belite suphoaluminate cement, which contains a certain CaSO₄ content without adding natural gypsum to the clinker. The sintering temperature, mineral composition, and the physical and mechanical properties of the cement clinkers were investigated. The techniques adopted included a comprehensive thermal analysis (DSC-TG), X-ray diffraction (XRD), X-ray fluorescence (XRF) and scanning electron microscopy (SEM). The results revealed that it is completely feasible to prepare high belite sulphoaluminate cement with the various industrial solid wastes mentioned above and the utilization rate of the solid wastes is up to 80%. The sintering temperature ranges from 1225 °C to 1350 °C, and the optimal sintering temperature is approximately 1300 °C. The clinkers prepared at 1300 °C set and harden quickly and have a slightly higher water requirement of normal consistency. The mechanical strength is greatly affected by the CaSO₄ and 3CaO·3Al₂O₃·CaSO₄ contents and the most reasonable CaSO₄ content is 15%.

Compared with nanosilica collected in a gaseous state, nanosilica sol has great economic value and application significance for improving the performance of concrete and mortar. In this study, the influence of nanosilica sol on the hydration process of different kinds of cement is studied by means of hydration heat analysis, X-ray diffraction analysis (XRD) and other methods, and the properties of mortar such as setting time, mechanical properties and porosity are also studied to characterize the influence of nanosilica sol on the macroscopic properties of mortar. The experimental results show that nanosilica sol can accelerate the hydration rate of two kinds of cement and promote the hydration reaction degree of cement, and this promotion effect increases with the increase in nanosilica sol content. At the same time, nanosilica sol can significantly shorten the setting time of the two kinds of cement, and it is more obvious with the increase in content. Excessive content of nanosilica sol will adversely affect the permeability resistance of mortar. It may be caused by the weak interval formed by nanosilica particle clusters in the mortar matrix, which can be supported by the mortar pore structure distribution test. At the same time, the influence of nanosilica sol on the hydration of the two kinds of cement is different, and the compressive strength of HBSAC cement mortar increases first and then decreases after adding nanosilica sol; However, the compressive strength of P·O 42.5 cement mortar increases gradually after adding nanometer silica sol. This shows that nanosilica sol does not effectively promote the hydration of β-C2S in high belite sulfoaluminate cement (HBSAC) mortar. Based on the above experimental results, it can be concluded that when the content of nanosilica sol is about 1%, it has the best promotion effect on the hydration of the two kinds of cement and the performance of mortar.

Due to the large amount of old hardened cement mortar attached to the surface of aggregate and the internal micro-cracks formed by the crushing process, the water absorption, apparent density, and crushing index of recycled coarse aggregate are still far behind those of natural coarse aggregate. Based on the performance requirements of different qualities of recycled coarse aggregate, the performance differences of recycled coarse aggregate before and after physical strengthening were observed. The results showed that the physical strengthening technique can remove old hardened mortar and micro powder attached to the surface of recycled coarse aggregate by mechanical action, which can effectively improve the quality of recycled coarse aggregate. The optimum calcination temperature of the recycled coarse aggregate was 400 °C and the grinding time was 20 min. The contents of the attached mortar in recycled coarse aggregates of Class I, II, and III were 7.9%, 22.8%, and 39.7%, respectively. The quality of recycled coarse aggregate was closely related to the amount of mortar attached to the surface. The higher the mortar content, the higher the water absorption, lower apparent density, and higher crushing index of the recycled coarse aggregate.

The high belite sulfoaluminate cement (HBSAC) containing CaSO₄, and without CaSO₄, based on solid wastes were successfully prepared from petroleum coke desulfurization slag (PCDS), fly ash (FA), carbide slag (CS), and bauxite (BX). The mineral composition of clinkers after different calcination history were investigated by X-ray fluorescence (XRF), X-ray diffraction (XRD)/Quantitative X-ray diffraction (QXRD), and scanning electron microscopy (SEM), so as to determine the calcination temperatures. The difference between residual CaSO₄ and dihydrate gypsum (DG) and the optimal content of residual CaSO₄ were discussed by studying the properties of HBSAC. The results revealed that the residual CaSO₄ in clinker could replace DG to participate in hydration, and showed some advantages in strength and early hydration heat, but meanwhile increased the water requirement of normal consistency and hydration heat at 72 h, and prolonged the setting time. With the increase of residual CaSO₄ content in clinker, the lower limit temperature of clinker formation gradually increased, and the crystal size of clinker minerals became finer and the boundary between crystals became more blurred. However, the optimal calcination temperature (1300 °C) of HBSAC clinker did not change. Considering the effect of residual CaSO₄ content on the water requirement of normal consistency, setting time, hydration heat, strength, and hydration products, the optimal design content of residual CaSO₄ in HBSAC clinker based on solid wastes, such as PCDS and FA, was 15%.

Alkaline electrolyzed water, a kind of clean green water with excellent characteristics such as high activity, strong alkalinity, high ion penetrating ability, electrical charge, and good molecule adsorption, was significant to the resource utilization of industrial fly ash waste. This paper studies highly active potassium-based alkaline electrolyzed water’s impact, compared with ordinary water, on the cement hydration process using microstructural methods such as a hydration heat test, differential thermal analysis, X-ray diffraction (XRD) pattern, and Scanning electron microscope (SEM) image analysis. Fly ash cement-based materials were first prepared with alkaline electrolyzed water as the mixing water. The alkaline electrolyzed water’s influence on fly ash paste workability and the mechanical properties of fly ash mortar for varying fly ash proportions were ratified. Then alkaline electrolyzed water with the best pH value was selected to prepare fly ash concrete, and its durability was studied. The test results showed that it is feasible to increase the utilization rate of fly ash by using alkaline electrolyzed water. Furthermore, it promoted the process of cement hydration, increased the rate of the hydration reaction, and the promotion effect increased with the increase in pH value of the alkaline electrolyzed water, and also promoted the effective decomposition of the vitreous shell of fly ash to stimulate its early activity. Concurrent tests with ordinary water paste showed that the water requirement for normal consistency and setting time with alkaline electrolyzed water paste were significantly less. Alkaline electrolyzed water also solved the problem related to the low early strength of fly ash mortar. Furthermore, using alkaline electrolyzed water with an optimum pH value of 11.5 to prepare fly ash concrete effectively reduced concrete’s carbonation depth and carbonation rate and lessened the chloride ion migration coefficient.

Green recycled aggregate concrete (RAC) with high strength and low shrinkage is prepared based on recycled coarse aggregate produced by the particle-shaping and aggregate-strengthening method and green low-carbon new cement. This not only effectively alleviates the shortage of natural resources, but also improves the performance of recycled aggregate concrete, which is of great significance for multi-channel resource utilization of construction waste. In this study, three kinds of recycled coarse aggregates (RCA), including simple crushing recycled coarse aggregate (JD-RCA), one-time particle-shaping recycled coarse aggregate (KL-RCA) and two-time particle-shaping recycled coarse aggregate (EKL-RCA), were prepared from the preparation technology of recycled aggregate, and high belite sulphoaluminate cement with excellent performance was used. The effects of aggregate quality, aggregate replacement ratio, and cementitious material content on mechanical properties and shrinkage properties of green recycled aggregate concrete were studied in comparison with ordinary Portland cement-based recycled aggregate concrete. The testing results show that the particle-shaping method can effectively improve the aggregate quality. The compressive strength and dry shrinkage performance of recycled aggregate concrete made of particle-shaped aggregate are only a little different from those of natural aggregate concrete, and even the performance of recycled aggregate is better than that of natural aggregate concrete under the condition of a low replacement ratio of recycled aggregate. In addition, high belite sulphoaluminate cement-based recycled aggregate concrete (HBRAC) not only has early strength and rapid hardening, but also has excellent drying shrinkage resistance, and its shrinkage rate can be reduced to more than 75% compared with ordinary Portland cement-based recycled aggregate concrete (OPRAC).