There is a constant drive to improve the properties of recycled concrete owing to its inferior strength and fracture toughness compared to normal concrete and recent progress in graphene oxide (GO) nanomaterials impelling nanosized reinforcements to recycled concrete. Here, GO-modified natural sand (NS)- or recycled sand (RS)-based mortars (GONMs or GORMs) with six GO fractions (w_GOs) were fabricated to explore their 28 d mechanical strengths (f²⁸_t, f²⁸_c), fracture toughness (K_IC, δ_c), and microhardness (H_v), as well as their crystal phases (using X-ray powder diffraction) and microstructures (using scanning electronic microscopy). Results reveal, greater enhancements in mechanical strengths (4.50% and 10.61% in f²⁸_t, 4.76% and 13.87% in f²⁸_c), fracture toughness (16.49% and 38.17% in K_IC, 160.14% and 286.59% in δ_c), and microhardness (21.02% and 52.70% in H_v) of GORM with just 0.025 wt‰ and 0.05 wt‰ GO, respectively, with respect to the control are achieved when comparing with those of GONM with the same w_GO. More zigzag surfaces, more irregular weak interface slips, and the relatively lower strengths of RS bring the superiority of the template and reshaping effects of GO into full play in GORM rather than in GONM. These outcomes benefit a wide range of applications of recycled concrete products.

The use of construction and demolition waste (CDW) to prepare recycled admixtures is of great significance for the complete resource reutilization of CDW. In this paper, different kinds of CDW were prepared into recycled powder (RP) with a specific particle size (0–45 µm or 0–75 µm). The fineness, water requirement ratio (WRR), fluidity, loss on ignition (LOI), strength activity index (SAI) and compatibility of cement and superplasticizer (CCS) were examined. The above test results were analyzed by advanced analysis tools, such as laser particle size analysis, XRD, XRF, DSC-TGA, SEM, and BET. The properties of different types of RPs varied greatly, which was closely related to the microstructure, particle morphology and chemical composition of the RP. The experimental results showed that all kinds of RPs after grinding had a high fineness and good particle size distribution, and the mineral composition was dominated by SiO₂ with the content exceeding 50%. The WRR of various RPs was between 105% and 112%, and the SAI was between 68% and 78%, but the LOI varied greatly. Different types of RPs had a negative impact on the CCS, but the compatibility of cement and naphthalene-based superplasticizer was less affected. The content of recycled brick powder (RBP) in a hybrid recycled powder (HRP) was an important factor. When the content of RBP in HRP exceeded 50%, the HRP could meet the basic performance requirements of fly ash.

In this study, a variety of industrial solid wastes, including petroleum coke desulfurization slag, fly ash and carbide slag with natural resource bauxite, were used as raw materials to prepare high belite suphoaluminate cement, which contains a certain CaSO₄ content without adding natural gypsum to the clinker. The sintering temperature, mineral composition, and the physical and mechanical properties of the cement clinkers were investigated. The techniques adopted included a comprehensive thermal analysis (DSC-TG), X-ray diffraction (XRD), X-ray fluorescence (XRF) and scanning electron microscopy (SEM). The results revealed that it is completely feasible to prepare high belite sulphoaluminate cement with the various industrial solid wastes mentioned above and the utilization rate of the solid wastes is up to 80%. The sintering temperature ranges from 1225 °C to 1350 °C, and the optimal sintering temperature is approximately 1300 °C. The clinkers prepared at 1300 °C set and harden quickly and have a slightly higher water requirement of normal consistency. The mechanical strength is greatly affected by the CaSO₄ and 3CaO·3Al₂O₃·CaSO₄ contents and the most reasonable CaSO₄ content is 15%.

Poor mechanical properties and durability of recycled aggregate concrete (RAC) hinder its application in the construction field. In this study, pre-wetted recycled coarse aggregate was used as the internal curing material for prepared RAC with low water-to-binder ratio (W/B), aiming to improve the mechanical properties and durability. The results show that the workability decreases with increasing contents of pre-wetted recycled coarse aggregate. The variation in compressive strength of RAC with different contents of pre-wetted recycled coarse aggregate is obvious within 28 d. After 28 d, the effect of internal curing of pre-wetted recycled coarse aggregate starts to occur, causing a sustained increase in compressive strength. The sealed concrete with 50% and 75% pre-wetted recycled coarse aggregate contents presents the highest compressive strength and better internal curing effect. The pre-wetted recycled coarse aggregate decreases the relative humidity inside the concrete and effectively inhibits the development of shrinkage in the early stages. The RAC with pre-wetted recycled coarse aggregate presents little effect on the drying shrinkage. Additionally, the electric flux of RAC cured for 28 d increases from 561C to 1001C, which presents good resistance to chloride permeation. Microscopic tests indicate that the incorporation of pre-wetted recycled coarse aggregate is beneficial to the improvements of internal structure of RAC.

Based on the characteristics of recycled concrete interface structures, a multi‐interface reconstruction model was established. To study the microstructure evolution of the interfacial transition zone (ITZ) during the carbonization process of recycled concrete, the microstructure characteristics of the ITZ of C30, C40, and C50 grade recycled concrete and the mortar matrix before and after carbonization were studied through the microhardness tester and SEM. The results show that the microhardness values of the ITZ and the mortar matrix are obviously increased and that the width of the ITZ decreases, while the ITZ performance of the C50 grade recycled concrete is not significantly changed. The ITZ exhibits a large amount of granular CaCO₃ after carbonization, the pores are refined, and microcracks are generated. Overall, there are significant differences in the microstructures between the ITZ and the mortar matrix before and after carbonization.

Energy efficiency is one of the important indicators for the evaluation of green buildings, and it is also related to the sustainable development of the building industry and energy conservation. Using agricultural waste in concrete to produce biomass recycled aggregates can effectively utilize agricultural solid waste to develop new wall materials with economic and energy-efficient properties. In this study, industrial wastes such as ground, granulated blast-furnace slag (GGBS) and fly ash (FA) were used to replace cement as cementitious material and coconut shell (CC) as lightweight coarse aggregate (LWA) in lightweight concrete. The lightweight coconut shell aggregate concrete with a density of less than 1950 kg/m³ was used as structural concrete. The thermal conductivity of synthesized biomass recycled aggregate concrete (SBRAC) was about 0.47 W/mK, which is 217% and 19% lower than that of natural aggregate concrete (NAC) and crushed coconut shell aggregate concrete (CCSAC), respectively. With the same volume, the costs of SBRAC and CCSAC are 25.1% and 4.9% lower than that of NAC, respectively.