Effective multiwalled carbon nanotube (MWCNT) fiber manufacturing methods have received a substantial amount of attention due to the low cost and excellent properties of MWCNTs. Here, we fabricated hybrid microfibers composed of hyaluronic acid (HA) and multiwalled carbon nanotubes (MWCNTs) by a wet-spinning method. HA acts as a biosurfactant and an ionic crosslinker, which improves the dispersion of MWCNTs and helps MWCNT to assemble into microfibers. The effects of HA concentration, dispersion time, injection speed, and MWCNT concentration on the formation, mechanical behavior, and conductivity of the HA/MWCNT hybrid microfibers were comprehensively investigated through SEM, UV-Vis spectroscopy, tensile testing, and conductivity testing. The obtained HA/MWCNT hybrid microfibers presented excellent tensile properties in regard to Young’s modulus (9.04 ± 1.13 GPa) and tensile strength (130.25 ± 10.78 MPa), and excellent flexibility and stability due to the superior mechanical and electrical properties of MWCNTs. This work presents an effective and easy-to-handle preparation method for high-performance MWCNT hybrid microfibers assembly, and the obtained HA/MWCNT hybrid microfibers have promising applications in the fields of energy storage, sensors, micro devices, intelligent materials, and high-performance fiber-reinforced composites.

Phthalonitrile–polyhedral oligomeric silsesquioxane (POSS) copolymers were prepared by adding two different POSS cage mixtures: epoxycyclohexyl POSS (EP0408) and N-phenylaminopropyl POSS (AM0281). The cure behavior and properties of these polymers were analyzed and compared using differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), dynamic mechanical analysis (DMA), Fourier transform far infrared (FTIR) measurements, and rheometric studies. The POSS-containing polymers showed higher chemical reactivity, better thermal stability and better mechanical performance in comparison to their unmodified counterparts. All the polymers showed water absorption below 1.5%. As revealed by FTIR measurements, the polymerization products contained triazine ring structures that were responsible for the superior thermal properties exhibited by these POSS-containing polymers.

Blends of cyanate ester and phthalonitrile–polyhedral oligomeric silsesquioxane copolymers were prepared, and their cure behavior and properties were compared via differential scanning calorimetry (DSC) analysis, thermogravimetric (TG) analysis, dynamic mechanical analysis, Fourier-transform far-infrared (FTIR) spectroscopy, and rheometric studies. The copolymer blends showed high chemical reactivity, low viscosity, and good thermal stability (TG temperatures were above 400 °C). The glass-transition temperature of the blends increased by at least 140 °C compared to cyanate ester resin. The blends are suitable for preparing carbon-fiber-reinforced composite materials via a winding process and a prepreg lay-up process with a molding technique. The FTIR data showed that the polymerization products contained triazine-ring structures that were responsible for the superior thermal properties.