The deformation of polymers at constant applied stress is one of their major drawbacks, limiting their use in advanced applications. The study of this property using classical techniques requires extensive testing over long periods of time. It is well known that reinforced polymers show improved behavior over time compared to their neat counterparts. In this study, the effect of adding different amounts of graphene nanoplatelets (GNPs) on the time‐dependent properties of high‐density polyethylene (HDPE) is investigated using short‐term creep tests and load/unload recovery tests. The results are discussed in terms of the test profile and the influence of loading history. Viscoplasticity/viscoelasticity analysis is performed using Zapas model and by comparing creep, creep compliance and pure viscoelasticity curves. The results show that the reinforcement of 15 wt% GNP have the most significant effect on the time‐dependent behavior, reducing the strain by more than 50%. The creep compliance curves show that nano‐reinforced HDPE behaves nonlinearly viscoelastically even at very low stresses. In addition to demonstrating the effect of nano‐reinforcement, the discussion of the results concludes that the influence of loading history can be quite significant and should not be neglected in the design and evaluation of material behavior.

This paper investigates the utilization of commercial masterbatches of graphene nanoplatelets to improve the properties of neat polymer and wood fiber composites manufactured by conventional processing methods. The effect of aspect ratio of the graphene platelets (represented by the different number of layers in the nanoplatelet) on the properties of high-density polyethylene (HDPE) is discussed. The composites were characterized for their mechanical properties (tensile, flexural, impact) and physical characteristics (morphology, crystallization, and thermal stability). The effect of the addition of nanoplatelets on the thermal conductivity and diffusivity of the reinforced polymer with different contents of reinforcement was also investigated. In general, the mechanical performance of the polymer was enhanced at the presence of either of the reinforcements (graphene or wood fiber). The improvement in mechanical properties of the nanocomposite was notable considering that no compatibilizer was used in the manufacturing. The use of a masterbatch can promote utilization of nano-modified polymer composites on an industrial scale without modification of the currently employed processing methods and facilities.

Due to the high interest in the use of glass/epoxy laminates in aerospace applications, aviation, and as cryogenic tanks, it is crucial to understand the behavior of composites under challenging environmental conditions. Polymer composites are exposed to low temperatures, including cryogenic temperatures, which can lead to the initiation of microdamage. This paper investigates damage initiation/accumulation and its influence on the properties of cross-ply woven glass fiber epoxy composites at low temperatures compared to room temperature conditions. To evaluate the influence of a low-temperature environment on the mechanical performance of glass fiber reinforced epoxy composite (GFRP) laminates, three types of test campaigns were carried out: quasi-static tensile tests and stepwise increasing loading/unloading cyclic tensile tests at room temperature and in a low-temperature environment (−50 °C). We demonstrated that the initial stiffness of the laminates increased at low temperatures. On the other hand, there were no observed changes in the type or mechanism of developed damage in the two test conditions. However, the reduction in stiffness due to the accumulated damage was more significant for the laminates tested at low temperatures (~17% vs. ~11%). Exceptions were noted in a few formulations where the extent of damage at low temperatures was insignificant (<1%) compared to that at room temperature. Since some of the studied laminates exhibited a relatively minor decrease in stiffness (~2–3%), we can also conclude that the formulation of matrix material plays an important role in delaying the initiation and formation of damage.

Continuous metalized regenerated cellulose fibers for advanced applications (e.g., multi-functional composites) are produced by electroless copper plating. Copper is successfully deposited on the surface of cellulose fibers using commercial cyanide-free electroless copper plating packages commonly available for the manufacturing of printed wiring boards. The deposited copper was found to enhance the thermal stability, electrical conductivity and resistance to moisture uptake of the fibers. On the other hand, the chemistry involved in plating altered the molecular structure of the fibers, as was indicated by the degradation of their mechanical performance (tensile strength and modulus).

Regenerated cellulose fibers coated with copper via electroless plating process are investigated for their mechanical properties, molecular structure changes, and suitability for use in sensing applications. Mechanical properties are evaluated in terms of tensile stiffness and strength of fiber tows before, during and after the plating process. The effect of the treatment on the molecular structure of fibers is investigated by measuring their thermal stability with differential scanning calorimetry and obtaining Raman spectra of fibers at different stages of the treatment. Results show that the last stage in the electroless process (the plating step) is the most detrimental, causing changes in fibers’ properties. Fibers seem to lose their structural integrity and develop surface defects that result in a substantial loss in their mechanical strength. However, repeating the process more than once or elongating the residence time in the plating bath does not show a further negative effect on the strength but contributes to the increase in the copper coating thickness, and, subsequently, the final stiffness of the tows. Monitoring the changes in resistance values with applied strain on a model composite made of these conductive tows show an excellent correlation between the increase in strain and increase in electrical resistance. These results indicate that these fibers show potential when combined with conventional composites of glass or carbon fibers as structure monitoring devices without largely affecting their mechanical performance.