While ω precipitates in metastable β titanium alloys are typically considered embrittling and consequently deleterious to the mechanical properties, this paper demonstrates that low-temperature aging (LTA) treatments for short time periods can in fact enhance the yield strength while preserving substantial elongation-to-failure in ω containing β titanium alloys. LTA treatments, carried out on a ductile β metastable Ti–12Mo alloy, significantly improve the yield strength of the material (∼55% increase as compared to solution-treated samples) while keeping both TRIP/TWIP effects and a large elongation-to-failure (ϵ = 0.4 in true strain), resulting in a balance of mechanical properties. IMPACT STATEMENT Employing a novel low-temperature annealing strategy, omega precipitates, typically considered embrittling in beta titanium alloys, can effectively increase the yield strength by 50% while preserving 40% tensile ductility. GRAPHICAL ABSTRACT

The magnetocaloric effect of Fe91−xMo8Cu1Bx (x=15,17,20) amorphous alloys has been studied. The temperature of the peak of magnetic entropy change can be tuned by altering the Fe∕B ratio in the alloy, without changing its magnitude, ∣ΔSMpk∣. The average contribution of the Fe atoms to ∣ΔSMpk∣ increases with increasing B content. This is correlated with the increase in the low temperature mean magnetic moment of Fe. A recently proposed master curve behavior for the magnetic entropy change is also followed by these alloys and is common for all of them.