Choline chloride (ChCl) / glycolic acid (GA) deep eutectic solvent (DES) media with high water content but without any additional catalyst are introduced in furfural and 5‐hydroxymethylfurfural (HMF) production. The effects of water content, reaction time, and reaction temperature are investigated with two feedstocks: a glucose/xylose mixture and birch sawdust. Based on the results, 10 equivalent quantities of water (32.9 wt.%) were revealed to be beneficial for conversions without rupturing the DES structure. The optimal reaction conditions were 160 °C and 10 minutes for the sugar mixture and 170 °C and 10 minutes for birch sawdust in a microwave reactor. High furfural yields were achieved, namely 62 % from the sugar mixture and 37.5 % from birch sawdust. HMF yields were low, but since the characterization of the solid residue of sawdust, after DES treatment, was revealed to contain only cellulose (49 %) and lignin (52 %), the treatment could be potentially utilized in a biorefinery concept where the main products are obtained from the cellulose fraction. Extraction of products into the organic phase (methyl isobutyl ketone, MIBK) during the reaction enabled the recycling of the DES phase, and yields remained high for three runs of recycling.

In this study, conversion of xylose to furfural was studied using lignin-based activated carbon-supported iron catalysts. First, three activated carbon supports were prepared from hydrolysis lignin with different activation methods. The supports were modified with different metal precursors and metal concentrations into five iron catalysts. The prepared catalysts were studied in furfural production from xylose using different reaction temperatures and times. The best results were achieved with a 4 wt% iron-containing catalyst, 5Fe-ACs, which produced a 57% furfural yield, 92% xylose conversion and 65% reaction selectivity at 170 °C in 3 h. The amount of Fe in 5Fe-ACs was only 3.6 µmol and using this amount of homogeneous FeCl₃ as a catalyst, reduced the furfural yield, xylose conversion and selectivity. Good catalytic activity of 5Fe-ACs could be associated with iron oxide and hydroxyl groups on the catalyst surface. Based on the recycling experiments, the prepared catalyst needs some improvements to increase its stability but it is a feasible alternative to homogeneous FeCl₃.