As a new textile fiber produced from Neosinocalamus affinis, the structures of the bamboo fiber were studied thoroughly in this research. Using Fourier-transform infrared (FTIR) (using a Micro-FTIR Spectrometer), X-ray diffraction (XRD), nuclear magnetic resonance (NMR) spectroscopy and scanning electron microscopy (SEM), we investigate the chemical composition, crystalline structure, molecular and morphology structure, respectively. Results show that the chemical composition of bamboo fiber is the same as all bast fibers, that is, cellulose constitutes the majority and lignin needs to be reduced further for textile applications. The bamboo fiber belongs to cellulose I crystalline structure as flax, cotton and ramie, while has a small molecular mass and a low degree of polymerization. The cross section of the single bamboo fiber is round with small lumen. It can be predicted that bamboo fiber has high breaking strength, but low elongation and has good water absorption properties. The structural characteristics of the bamboo fiber are different from those of other textile plant fibers.

Bamboo fibers (BFs)-reinforced epoxy resin (EP) composites are prepared by resin transfer molding (RTM). The influence of BFs surface modification (NaOH solution or coupling agents, i.e., KH550 and KH560) on interfacial properties of BFs/EP composites is systematically investigated. The synergistic effect of hydrolysis, peeling reaction of BFs, and the condensation reaction of hydrolyzed coupling agents are confirmed by FTIR. Scanning electron microscopy (SEM) and atomic force microscopy (AFM) reveal that the interfacial compatibility of NaOH- and silane-modified BFs/EP composites was significantly improved. KH550-modified BFs/EP composite renders optimal tensile, flexural, and impact strength values of 68 MPa, 86 MPa, and 226 J/m. The impact resistance mechanism at the interface of BFs/EP composites was proposed. Moreover, the dynamic mechanical properties, creep behavior, and differential scanning calorimetry of BFs/EP composites have also been carried out to understand thermal stabilities. Overall, the surface-modified BFs-reinforced EP composites exhibited superior interfacial bonding.