In this paper, the initial values of damage parameters in the Gurson–Tvergaard–Needleman (GTN) model are determined by a microscopic test combined with empirical formulas, and the final accurate values are determined by finite element reverse calibration. The original void volume fraction (f₀), the volume fraction of potential nucleated voids (f_N), the critical void volume fraction (f_c), the void volume fraction at the final failure (f_F) of material are assigned as 0.006, 0.001, 0.03, 0.06 according to the simulation results, respectively. The hemispherical punch stretching test of commercially pure titanium (TA1) sheet is simulated by a plastic constitutive formula derived from the GTN model. The stress and strain are obtained at the last loading step before crack. The forming limit diagram (FLD) and the forming limit stress diagram (FLSD) of the TA1 sheet under plastic forming conditions are plotted, which are in good agreement with the FLD obtained by the hemispherical punch stretching test and the FLSD obtained by the conversion between stress and strain during the sheet forming process. The results show that the GTN model determined by the finite element reverse calibration method can be used to predict the forming limit of the TA1 sheet metal.

Multiple phase transformations were carried out during dehydrogenation process of TiH2-based powder metallurgy. The influence of phase transformation on the microstructure is highly worthy of attention. In situ synchrotron radiation was employed to investigate the phase transformation sequence of TiH2 powder compact during the vacuum sintering process. It was found that a transformation route TiH1.971 → TiH2 + TiH + TiH0.71 + α(H) → TiH + TiH0.71 + α(H) → TiH + TiH0.71 + α(H) + β(H) → α(H) → α took place, resulting in an equiaxed microstructure. Increasing heating rate and avoiding the intense dehydrogenation to retain hydrogen-rich β (β(H)) and TiHx aciculae at the interfaces is found to be a feasible method to fabricate hierarchical α-Ti structures. A fully dense fine martensitic microstructure was produced after fast heating the TiH2 powder compact to 1100 °C and an immediate hot extrusion. Subsequently, by vacuum annealing treatment at 700 °C, composite α/βt lamellar structures were generated and a simultaneously enhanced tensile strength of 746 MPa and excellent elongation to fracture of 33.8% were achieved. It is suggested that adjusting the dehydrogenation reactions of TiH2-based powder metallurgy is conductive to generating hierarchical lamellar structures with a highly promising combination of strength and ductility for pure Ti.