The development of Alumina-Forming Austenitic (AFA) stainless steel is reviewed in this paper. As a new type of heat-resistant steel, AFA steel forms an alumina protective scale instead of chromia in a corrosive environment. This work summarizes the types of developed AFA steels and introduces the methods of composition design. Various precipitates appear in the microstructure that directly determine the performance at high temperatures. It was found that alloy elements and the heat treatment process have an important influence on precipitates. In addition, the corrosion resistance of AFA steel in different corrosive environments is systematically analyzed, and the beneficial or harmful effects of different elements on the formation of alumina protective scale are discussed. In this paper, the short-term mechanical properties, creep properties and influencing factors of AFA steel are also analyzed. This work aims to summarize the research status on this subject, analyze the current research results, and explore future research directions.

Anisotropy is the difference in the microstructure or mechanical properties of materials in different directions. Anisotropic behavior occurs in rolled sheets, and this anisotropy is very obvious in laminated composites. In this work, the influence of anisotropy on the microstructure and mechanical properties of Ti/Al laminated composites fabricated by rolling was investigated. The results show that the microstructure and mechanical properties of the Ti/Al laminated composites were obviously anisotropic. The grains in the Al layer of the composites were elongated along the rolling direction and were compressed perpendicular to the rolling direction. The grains in the Ti layer of the composites had no obvious preferential orientation and comprised mainly twins. With the rolling direction as 0°, the mechanical properties of the Ti/Al laminated composites varied greatly as the angle of the composites increased. The tensile strength, elongation and bond strength of the Ti/Al laminated composites decreased with increasing angle of the composites. In addition, the microhardness of the Ti/Al laminated composites increased with increasing angle of the composites.

In this paper, the initial values of damage parameters in the Gurson–Tvergaard–Needleman (GTN) model are determined by a microscopic test combined with empirical formulas, and the final accurate values are determined by finite element reverse calibration. The original void volume fraction (f₀), the volume fraction of potential nucleated voids (f_N), the critical void volume fraction (f_c), the void volume fraction at the final failure (f_F) of material are assigned as 0.006, 0.001, 0.03, 0.06 according to the simulation results, respectively. The hemispherical punch stretching test of commercially pure titanium (TA1) sheet is simulated by a plastic constitutive formula derived from the GTN model. The stress and strain are obtained at the last loading step before crack. The forming limit diagram (FLD) and the forming limit stress diagram (FLSD) of the TA1 sheet under plastic forming conditions are plotted, which are in good agreement with the FLD obtained by the hemispherical punch stretching test and the FLSD obtained by the conversion between stress and strain during the sheet forming process. The results show that the GTN model determined by the finite element reverse calibration method can be used to predict the forming limit of the TA1 sheet metal.

Multiple phase transformations were carried out during dehydrogenation process of TiH2-based powder metallurgy. The influence of phase transformation on the microstructure is highly worthy of attention. In situ synchrotron radiation was employed to investigate the phase transformation sequence of TiH2 powder compact during the vacuum sintering process. It was found that a transformation route TiH1.971 → TiH2 + TiH + TiH0.71 + α(H) → TiH + TiH0.71 + α(H) → TiH + TiH0.71 + α(H) + β(H) → α(H) → α took place, resulting in an equiaxed microstructure. Increasing heating rate and avoiding the intense dehydrogenation to retain hydrogen-rich β (β(H)) and TiHx aciculae at the interfaces is found to be a feasible method to fabricate hierarchical α-Ti structures. A fully dense fine martensitic microstructure was produced after fast heating the TiH2 powder compact to 1100 °C and an immediate hot extrusion. Subsequently, by vacuum annealing treatment at 700 °C, composite α/βt lamellar structures were generated and a simultaneously enhanced tensile strength of 746 MPa and excellent elongation to fracture of 33.8% were achieved. It is suggested that adjusting the dehydrogenation reactions of TiH2-based powder metallurgy is conductive to generating hierarchical lamellar structures with a highly promising combination of strength and ductility for pure Ti.