Four polymer and ceramic computer-aided design/computer-aided manufacturing (CAD/CAM) materials from different manufacturers (VITA CAD-Temp (polymethyl methacrylate, PMMA), Celtra Duo (zirconia-reinforced lithium silicate ceramic, ZLS), IPS e.max CAD (lithium disilicate (LS₂)), and VITA YZ (yttrium-tetragonal zirconia polycrystal, Y-TZP)) were tested to evaluate the cytotoxic effects and collagen type I secretions on human gingival fibroblasts (HGFs). A total of 160 disc-shaped samples (Ø: 10 ± 2 mm; h: 2 mm) were milled from commercial blanks and blocks. Direct-contact cytotoxicity assays were evaluated at 24, 48, and 72 h, and collagen type I (COL1) secretions were analysed by cell-based ELISA at 24 and 72 h. Both experiments revealed statistically significant differences (p < 0.05). At 24 and 48 h of contact, cytotoxic potential was observed for all materials. Later, at 72 h, all groups reached biologically acceptable levels. LS₂ showed the best results regarding cell viability and collagen secretion in all of the time evaluations, while Y-TZP and ZLS revealed intermediate results, and PMMA exhibited the lowest values in both experiments. At 72 h, all groups showed sharp decreases in COL1 secretion regarding the 24-h values. According to the results obtained and the limitations of the present in vitro study, it may be concluded that the ceramic materials revealed a better cell response than the polymers. Nevertheless, further studies are needed to consolidate these findings and thus extrapolate the results into clinical practice.

Yttria-stabilized tetragonal zirconia polycrystal (Y-TZP) and polymethyl methacrylate (PMMA) are used very often in dentistry. Y-TZP is the most widely used zirconia dental ceramic, and PMMA has classically been used in removable prosthesis manufacturing. Both types of materials are commercialized in CAD/CAM system blocks and represent alternatives for long-lasting temporary (PMMA) or definitive (Y-TZP) implantological abutments. The aim of the present work is to reveal that human gingival fibroblasts (HGFs) have a favorable response when they are in contact with Y-TZP or PMMA as a dental implant abutment or implant-supported fixed prosthesis, and also to review their principal characteristics. We conducted an electronic search in the PubMed database. From an initial search of more than 32,000 articles, the application of filters reduced this number to 5104. After reading the abstracts and titles, we reduced the eligible articles to 23. Ultimately, we have included eight articles in this review.

This study is a contribution to our understanding of the mechanical behaviour of dental implants through the use of the finite element and the photoelastic methods. Two internal connection and bone level dental implants with different design have been analysed (M-12 by Oxtein S.L., Zaragoza, Spain, and ASTRA, from Dentsply Sirona, Charlotte, NC, USA), evaluating the stress distribution produced by axial stresses and a comparison has been established between them, as well as between the two methods used, in order to validate the adopted hypotheses and correlate the numerical modelling performed with experimental tests. To load the implant in laboratory testing, a column was placed, such that the loading point was about 9.3 mm from the upper free surface of the resin plate. This column connects the implant with the weights used to define the test load. In turn, support for both plates was achieved by two 6 mm bolts 130 mm apart and located on a parallel line with the resin (flush with the maximum level of the implant), at a depth of 90 mm. The results obtained with both methods used were similar enough. The comparison of results is fundamentally visual, but ensures that, at least in the range of forces used, both methods are similar. Therefore, the photoelastic method can be used to confirm in a real way the virtual conditions of the finite element models, with the implications in the investigation of dental implants that this entails.

Polymethyl methacrylate (PMMA) and lithium disilicate are widely used materials in the dental field. PMMA is mainly used for the manufacture of removable prostheses; however, with the incorporation of CAD-CAM technology, new applications have been introduced for this material, including as a provisional implant attachment. Lithium disilicate is considered the gold standard for definitive attachment material. On the other hand, PMMA has begun to be used in clinics as a provisional attachment until the placement of a definitive one occurs. Although there are clinical studies regarding its use, there are few studies on cell reorganization around this type of material. This is why we carried out an in vitro comparative study using discs of both materials in which human gingival fibroblasts (HGFs) were cultured. After processing them, we analyzed various cellular parameters (cell count, cytoskeleton length, core size and coverage area). We analyzed the surface of the discs together with their composition. The results obtained were mostly not statistically significant, which shows that the qualities of PMMA make it a suitable material as an implant attachment.

Immediate implant placement protocols after dental extraction have enabled a reduction in surgical phases. This procedure has increased patient satisfaction and similar survival rates to late implant placement procedures. However, placing an implant immediately after dental extraction does not counteract the physiological remodeling of alveolar bone. For this reason, additional surgical techniques have been developed, such as the placement of a connective tissue graft (CTG) or the socket shield technique (SST). Dimensional changes in the peri-implant tissues were observed after placement of immediate implants following the extraction and CTG and/or SST. A total of 26 surgical interventions were carried out in which dimensional change variables of peri-implant tissues were analyzed. The preoperative state and immediate postoperative situation were compared with the situation after one year. Measurements were taken at 3, 5, and 7 mm from the gingival margin and analyzed in this CBCT radiological study (Planmeca Promax 3D). The implant platform was used as a reference point for the measurement of changes in alveolar crest height. One year after performing either of the two techniques (CTG and/or SST), a significant increase in the gingiva thickness and vestibular cortex occurred at 5 mm (0.65 ± 1.16 mm) and 7 mm (0.95 ± 1.45 mm) from the gingival margin. Additionally, an increase in thickness of palatal bone was registered at 3 mm (0.48 ± 0.90 mm). The graft placement group showed an increase in thickness of peri-implant tissue in the vestibular area after one year, although CTG and SST groups were clinically similar. The implementation of SST revealed promising results regarding the buccal thickness of hard and soft tissues after one year. A significant increase in vestibular cortical bone thickness, as well as the overall mucosa thickness and buccal bone at 3 mm from the gingival margin, was observed. A significant reduction in the distance from the bone crest to the platform was detected in both techniques. Both techniques (CTG and SST) are appropriate to provide sufficient volume to peri-implant tissues in the vestibular area of anterior maxillary implants. Some limitations were detected, such as the lack of an aesthetic analysis or small sample size, so results should be interpreted with caution. Future studies are necessary to further evaluate the long-term predictability of these techniques.