Platinum (Pt)-based nanoparticle metals have received a substantial amount of attention and are the most popular catalysts for direct methanol fuel cell (DMFC). However, the high cost of Pt catalysts, slow kinetic oxidation, and the formation of CO intermediate molecules during the methanol oxidation reaction (MOR) are major challenges associate with single-metal Pt catalysts. Recent studies are focusing on using either Pt alloys, such as Fe, Ni, Co, Rh, Ru, Co, and Sn metals, or carbon support materials to enhance the catalytic performance of Pt. In recent years, Pt and Pt alloy catalysts supported on great potential of carbon materials such as MWCNT, CNF, CNT, CNC, CMS, CNT, CB, and graphene have received remarkable interests due to their significant properties that can contribute to the excellent MOR and DMFC performance. This review paper summaries the development of the above alloys and support materials related to reduce the usage of Pt, improve stability, and better electrocatalytic performance of Pt in DMFC. Finally, discussion of each catalyst and support in terms of morphology, electrocatalytic activity, structural characteristics, and its fuel cell performance are presented.

Due to growing environmental concerns and regulations limiting the use of harmful and toxic synthetic corrosion inhibitors, there is a high demand for sustainable corrosion inhibitors. In this study, a green and rapid technique was used to synthesize amide N-(4-aminobutyl)palmitamide (BAPA) which yielded 91.17% of the product within 2 min, compared to a low yield of 75-80% and a very long 8-10 h reaction time with the conventional thermal condensation method. The chemical structure of BAPA was analyzed by FT-IR, 1HNMR and 13CNMR spectra, as well as CHNS elemental analysis. When applied to mild steel exposed to 1 M HCl, BAPA delayed and reduced corrosion by adsorbing to the steel surface to form a protective layer. The inhibition efficiency increased with increasing amide concentration, and maximal inhibition of 91.5% was observed at 0.5 mM BAPA. The adsorption of BAPA on mild steel in an acidic solution was studied and inhibition performance was correlated with the calculated adsorption-free energy ΔGads, indicating good agreement between the experimental and adsorption findings. Surface morphology of untreated and treated mild steel coupons was evaluated by SEM, and based on density functional theory (DFT) computations and atomic charges analysis, a stronger interaction was observed between BAPA and mild steel surface leading to the formation of a compact protective film on the metallic surface. This protective film is attributed to the presence of nitrogen atoms and carbonyl group in the chemical structure of BAPA.