As a state-of-the-art method, the digital image correlation (DIC) technique is used to capture the fracture properties of wood along the longitudinal direction, such as the crack propagation, the strain field, and the fracture process zone (FPZ). Single-edge notched (SEN) specimens made of Douglas fir (Pseudotsuga menziesii) from Canada with different notch-to-depth ratios are tested by three-point-bending (3-p-b) experiment. The crack mouth opening displacements (CMOD) measured by the clip gauge and DIC technique agree well with each other, verifying the applicability of the DIC technique. Then, the quasi-brittle fracture process of wood is analyzed by combing the load-CMOD curve and the strain field in front of the preformed crack. Additionally, the equivalent elastic crack length is calculated using the linear superposition hypothesis. The comparison between the FPZ evolution and the equivalent elastic crack shows that specimens with higher notch-to-depth ratios have better cohesive effect and higher cracking resistance.

Ultrahigh toughness cementitious composites are a kind of high-performance cementitious material with a characteristic of ductile fracture. Based on the continuum damage mechanics theory and flexural fatigue damage model, two damage propagation models of ultrahigh toughness cementitious composites are built. One is a linear bilogarithmic model with J-integral range as its independent variable, while the other one is a linear model on a semilogarithmic scale with fatigue stress level as its independent variable. However, according to former research, the J-integral depends strongly on specimens’ geometry, so the first damage propagation model is deeply influenced by material dimension. As a result, the second damage propagation model is more convenient in application, shows the material fatigue property in comparison with the first model. In order to prove these two models and obtain the parameters, a three-point flexural fatigue experiment on single-edge-notched fracture specimens is carried out. The results shows that the two models fit better with the experimental results, rather than the crack propagation law of ultrahigh toughness cementitious composites.