Coffee ground waste from the coffee beverage preparation is mainly discarded and consequently ends up in landfill, which cause the contamination of caffeine in various environmental compartments. This study focuses on the upcycling of coffee-ground waste to carbon quantum dots (CQDs) for use as a modifying material to improve the visible light activity of titanium dioxide (TiO₂). The CQD solution was synthesized by hydrothermal method, which has an average size of 2.80 ± 0.63 nm. The CQDs/TiO₂ photocatalysts were prepared by combining CQD solutions at various amounts with sol-gel TiO₂ and then coated on the fiberglass cloths (FGCs). The photocatalytic application mainly focuses on the removal of caffeine from the water. The photocatalytic experiment was preliminary run in a simple batch reactor under visible light. The 5CQDs/TiO₂ coated FGC (5 mL of CQD solution/g of Ti-based on sol-gel) showed the best performance, and it was selected for the removal of caffeine and other pharmaceuticals (i.e., carbamazepine and ibuprofen) in the recirculating reactor. The removals of caffeine, carbamazepine, and ibuprofen after irradiation for 9 h were 82%, 88%, and 84%, respectively. The residual concentrations were significantly lower than the reported toxicity levels based on specific species. The changes in total organic carbon were observed, indicating the mineralization of pharmaceuticals in water. The 5CQDs/TiO₂ coated FGC showed good flexible performance. No obvious loss of activity was observed for five runs. The actual wastewater from the coffee pot cleaning process was also tested. The removal was 80% for caffeine and 86% for color in the unit of the American Dye Manufacturers Institute (ADMI).

Struvite (MgNH₄PO₄·6H₂O) is normally used as a fertilizer in agriculture, where struvite crystallization from hydrolysed human urine is a simple and reliable method for phosphorus (P) recovery. Human urine, however, contains high amount of pharmaceuticals, which may cause health risk for applications. This research investigates the possibility of decreasing the amount of pharmaceuticals (tetracycline, demeclocycline and oxytetracycline) in struvite crystals recovered from synthetic and human urines by focusing on storage time, and of increasing the quality of struvite production. Urines were stored for different times up to 15 days prior to recovery of phosphorus by two steps, spontaneous precipitation and struvite crystallization. The morphology of spontaneous precipitates and struvite crystals was observed. Spontaneous precipitation removed around 17–24% of phosphate from synthetic and human urines, while pharmaceuticals were removed with a quite high amount at a short storage time (5 days) and this amount decreased with increasing the storage time (10 and 15 days). Urines with>70% remaining phosphates were re-used for struvite crystallization by adding extra magnesium. It was found that maximum P-recovery efficiency could be achieved from struvite crystallization at 5-day storage time, 70% and 68% of remaining P in the separated supernatant from synthetic and human urines, respectively, whereas less than 1% pharmaceuticals remained in the struvite crystals from both samples. This indicates that the procedure in this work is a good method for phosphorus recovery, in which high struvite purity (>99%) is obtained with low amount of pharmaceuticals.

This work presents the development of titanium dioxide (TiO₂) film immobilized on circular glass sheets for photocatalytic degradation of caffeine under ultraviolet C (UVC) irradiation. TiO₂ was synthesized through the ultrasonic-assisted sol–gel method and immobilized on circular glass sheets by the doctor blade technique. Polyvinylpyrrolidone (PVP) was used to mix with the TiO₂ precursor solution to enhance film adhesion on the glass surface. TiO₂ film was mainly composed of anatase phase with a small amount of rutile phase. Caffeine removal was found to increase with increasing irradiation time. Caffeine (20 mg/L) in the synthetic wastewater could not be detected after 3 h of UVC irradiation. The reaction rate of caffeine degradation followed the pseudo-first-order model. The concentrated caffeine solutions required a longer irradiation time for degradation. The used TiO₂-coated glass sheets could be easily separated from the treated wastewater and reusable. The caffeine removal efficiency of TiO₂-coated glass sheets in each cycle maintained a high level (~100%) during fifteen consecutive cycles.

Background: TiO₂ has been proved as an effective photocatalyst for air purification that can produce hydroxyl radicals and superoxide radicals by the illumination of light with suitable energy. These radicals are extremely powerful agents in the degradation of gaseous pollutants. A major drawback of TiO₂ is its wide energy band gaps of 3.2 and 3.0 eV for anatase and rutile phases, respectively, which are mostly equivalent to the photon wavelength absorption in the range of UV region. Methods: The modification strategies of TiO₂ as photocatalysts for air treatment, such as metal doping, non-metal doping, co-doping, and coupling with other semiconductors are discussed. The photocatalytic performance of the pristine TiO₂ and modified TiO₂ for degradations of gaseous pollutants are reviewed. Results: Various parameters can affect the photocatalytic removal efficiencies of gaseous pollutants, such as the initial concentration of pollutants, relative humidity, light source, irradiation time, and the preparation of TiO₂ photocatalysts. The optimal content of dopants and the combinedsemiconductors should be considered for preventing the recombination of electrons and holes during irradiation. Conclusion: Doping with heteroatoms and coupling could enhance the photocatalytic activity of TiO₂. The modified photocatalysts could be applied for photocatalytic degradation of gaseous pollutants, including volatile organic compounds (VOCs), nitrogen oxides (NO_x), and sulfur oxides (SO_x).

Biomass conversions to chemicals via various conventional technologies require high energy consumption, high temperature, high pressure, or high system cost. Alternatively, photocatalysis is one of the greener technologies because it utilizes the energy from lamps or natural sunlight with catalysts to synthesize chemicals under mild conditions and room temperature. In this work, zinc oxide (ZnO) particles were successfully synthesized using polyvinylpyrrolidone as an additive in coprecipitation to control the size and protect the aggregation. The crystal structure of hexagonal wurtzite was found in the obtained nanoparticles. The photocatalytic activities of the obtained samples were evaluated for the production of high-value chemicals (gluconic acid, xylitol, arabinose, and formic acid) via the photocatalytic conversion of glucose under UV-A irradiation. The photocatalytic results indicated the relationship of defects (i.e., oxygen vacancies and zinc vacancies) with glucose conversions. From the ZnO nanoparticles calcined at various temperatures from 400 to 700 °C, the one calcined at 700 °C showed the highest glucose conversion of 21.5% with a high yield of carboxylic acid products (gluconic acid and formic acid). The gluconic acid showed the highest yield of 15% for 180 min, while the formic acid, arabinose, and xylitol presented the highest yields of 7, 1, and 0.5% for 180 min, respectively. Pure ZnO nanoparticles can convert glucose into value-added products without adding an acid or base in the reaction.