Low-density polyethylene (LDPE) composites reinforced with finely powdered waste glass were identified as a potential material for 3D printed structures for use in low-duty frictional applications. A recently published 3D printing model was used to calculate the limits in the filament feed rate and printing speed. Tribological tests (pin-on-disc method) of the printed composites were performed for different print-path directions. Differential scanning calorimetry (DSC) was performed on the samples and the composites showed a higher crystallinity compared with LDPE, which partially explains the higher elastic modulus of the composites determined during static tensile tests. Using a fine glass powder as reinforcement improved the wear resistance of LDPE by 50% due to the formation of a sliding film on the sample’s surface. An evident effect of friction direction vs. the printed path direction on wear was found; which was likely related to differences in the removal of friction products from the friction area for different print-path directions. The LDPE composites with fine waste glass particles are promising materials for low-duty frictional applications and should be the subject of further research.

This work is devoted to evaluating the effectiveness of the recovery of carbon fibers from end-of-life wind turbine blades in the pyrolysis process, and the use of those fibers in the production of flat composite panels. The recovery of carbon fibers from wind turbine blades uses a pyrolysis process at 500–600 °C in a non-oxidizing atmosphere, in such a way that makes it possible to preserve the shape and dimensions of the fibers. Using recycled carbon fibers, flat CFRP sheets with epoxy resin matrix were produced by pressing. Seven different series of samples were tested, which differed in fiber length, fiber orientation, and pressure holding time. The results obtained on the recycled fibers were compared to the original carbon fibers, cut to corresponding lengths. Additionally, one of the series was reinforced with a biaxial fabric. The most favorable pressing parameters are empirically found to be pre-pressing 2 MPa (10 min), and further pressing at a pressure of 7 MPa until the resin completely cross-linked (about 120 min). A number of tests were carried out to demonstrate the usefulness of pyrolytic fibers, including tensile strength of carbon fibers, bending strength, SEM observations, FT-IR, and Raman spectroscopy. The tests carried out on the carbon fibers show that the pyrolysis process used leaves about 2% of the matrix on the surface of the fiber, and the tensile strength of the fibers drops by about 20% compared to the new carbon fibers. The research results show that the use of the recycled carbon fibers in the production of flat composite plates is reliable, and their mechanical properties do not differ significantly from plates made of corresponding original carbon fibers. Composite panels with the pyrolytic fibers (274 MPa) show up to a 35% higher flexural strength than similarly produced panels with the original new carbon fibers (203 MPa), which means that the panels can be used in the production of elements for footbridges, bridges, pipelines, or structural elements of buildings and roofing.

In this paper, we investigated theimpact of glassy carbon (GC) reinforcement oncrystal structure and the mechanical performance of high-density polyethylene (HDPE). We made composite samples by mixing HDPE granules with powder in ethanol followed bymelt mixing in a laboratory extruder. Along with the investigated composite, we also prepared samples with carbon nanotubes (CNT), graphene (GNP) and graphite (Gr) to compare GC impact with already used carbon fillers. To evaluate crystal structure and crystallinity, we used X-ray diffraction (XRD) and differential scanning calorimetry (DSC). We supported the XRD results with a residual stress analysis (RSA) according to the EN15305 standard. Analysis showed that reinforcing with GC leads to significant crystallite size reduction and low residual stress values. We evaluated the mechanical properties of composites with hardness and tensile testing. The addition of glassy carbon results inincreased mechanical strength incomposites with CNT and GNP.

In this study, the influence of different carbon fillers on the tribological and manufacturing properties of the thermoplastic polyamide PA6 is presented. The following materials were used as carbon additives: glassy carbon (GC), carbon obtained from the pyrolysis of polymer wastes (BC), and graphene oxide (GO). Fillers were introduced into the PA6 matrix by mechanical stirring in alcohol to settle carbon particles onto the granule surface. Samples were made by injection molding from the produced granules. The microstructure, hardness, and melt flow index (MFI) of the prepared materials were determined. Also, the degree of crystallinity of the samples was examined by Differential Scanning Calorimetry (DSC) and X-ray Diffraction (XRD). The melting point (Tm) was examined using DSC, the results from which allowed the correct heat treatment of PA6 to increase the crystallinity of the obtained material to be selected. The dry sliding tribological behavior of the composites was evaluated via pin-on-block tests against cast iron counterparts. The tests were performed at room temperature, with a sliding speed 0.1 m/s, a sliding distance of 250 m, and a normal force of 40 N. The obtained results revealed that the introduction of GO into the PA6 matrix provides favorable wear behavior, such as the formation of debris that acts as rollers that give a decrease in wear and a lower coefficient of friction. The coefficient of friction in samples with graphene oxide was nearly two times lower than with other samples. However, the ease of manufacture of this material was drastically reduced compared to GC or BC fillers. Microstructural investigations of wear tracks revealed poor adhesion between the polymer matrix and micrograins of carbon fillers (GC and BC), and therefore their influence on tribological properties was less compared to graphene oxide.

One of the most important directions in the development of additive manufacturing or three-dimensional (3D) printing technologies is the creation of functional materials, which allow not only prototyping but also the manufacturing of products with functional properties. In this paper, poly-lactide acid (PLA) /carbon black (CB) composites with segregated (ordered) structure have been created. Computer simulation based on the Mamunya geometrical model showed that the CB content within φ = 2.5–5 vol.% in the polylactide matrix leads to the formation of a continuous electrically conductive phase with an increase of electrical conductivity σ_dc above the percolation threshold. The simulation results were experimentally confirmed by optical microscopy and studies of the electrical conductivity of the composites. It was found that increasing CB content from φ = 1 vol.% to φ = 7 vol.% in the composites causes insignificant (due to the segregated structure) phase changes in the polylactide matrix and improves the thermal properties of composites. Electrically conductive filaments for Fused Deposition 3D Printing (FDM) were developed from PLA/CB composites and then 3D printed. A correlation between the electrical conductivity σ_dc and the CB content φ for base composites, filaments produced from them, and final 3D samples, has been found. Conductivity varies within σ_dc = 3.1·10⁻¹¹ − 10·10⁻³ S/cm for the filaments and σ_dc = 3.6·10⁻¹¹ − 8.1·10⁻⁴ S/cm for the final 3D-products.

The aspect of drug delivery is significant in many biomedical subareas including tissue engineering. Many studies are being performed to develop composites with application potential for bone tissue regeneration which at the same provide adequate conditions for osteointegration and deliver the active substance conducive to the healing process. Hydroxyapatite shows a great potential in this field due to its osteoinductive and osteoconductive properties. In the paper, hydroxyapatite synthesis via the wet precipitation method and its further use as a ceramic phase of polymer–ceramic composites based on PVP/PVA have been presented. Firstly, the sedimentation rate of hydroxyapatite in PVP solutions has been determined, which allowed us to select a 15% PVP solution (sedimentation rate was 0.0292 mm/min) as adequate for preparation of homogenous reaction mixture treated subsequently with UV radiation. Both FT-IR spectroscopy and EDS analysis allowed us to confirm the presence of both polymer and ceramic phase in composites. Materials containing hydroxyapatite showed corrugated and well-developed surface. Composites exhibited swelling properties (hydroxyapatite reduced this property by 25%) in simulated physiological fluids, which make them useful in drug delivery (swelling proceeds parallel to the drug release). The short synthesis time, possibility of preparation of composites with desired shapes and sizes and determined physicochemical properties make the composites very promising for biomedical purposes.