The distribution homogeneity of grain size affects the fluidity of the semi-solid slurry, which in turn affects the properties of the casting. One key factor affecting grain size uniformity resides in the nucleation number, which has been studied thoroughly, while the other factor is temperature gradient which has not been investigated yet. In this study, the microstructure evolutions under certain temperature gradients are investigated by experiment and simulation using a two-dimensional quantitative phase-field (PF) model. A parallel and adaptive mesh refinement algorithm is adopted to solve the nonlinear phase-field equations. The results indicate that temperature gradient can affect the size distribution of microstructure in the semi-solid slurry prepared by the SEED process. A higher temperature gradient (in the range of 0.230~0.657 °C/mm) along the radial direction is beneficial to the homogeneity of the grain size in a slurry.

Application of a coating on a mold surface is widely used in the foundry industry. Changes in coating change the heat transfer at the mold–melt interface, which influences the microstructure of the casting. In this study, the effect of boron nitride coating thickness on the interfacial heat transfer and slug microstructure in the Swirled Enthalpy Equilibration Device (SEED) process was investigated. The temperatures of the semi-solid slug and mold were measured, and the interfacial heat transfer coefficient and heat flux of the mold–slug interface was estimated based on these data. Microstructures of the quenched slugs were also examined. The results indicated that the interfacial heat transfer coefficient decreased with an increase in coating thickness and was sensitive to a coating thickness of less than 0.1 mm. The interfacial heat flux decreased sharply at the early stage, and then slowed down as the swirling time increased and the coating thickened. The coating thickness affected the temperature evolution of the slug at the early stage of the SEED process. As the coating thickness increased from near zero to 1.0 mm, the grain size of the slug increased by ~20 µm and the globular structure of the slug transformed into a dendritic structure.