The aim of this study was to evaluate the production of microbial cellulose films (MCFs) in culture media based on green tea and different carbon sources, using two microbial consortia (COr and CFr). During the fermentation process, there was a reduction in the total soluble solids (TSS) content and pH, as well as an increase in the acidity in all treatments. Furthermore, fluctuations in the total sugar content and proteins during the fermentation process were associated with the consumption of carbon and nitrogen sources, as well as the production of MCFs. In the color analysis, a decrease in the L* value was observed while the rest of the parameters remained stable. Production of films was observed between days 6 and 9 of fermentation; the preferred substrate for COr was glucose (wet base yields = 603.61% and dry base yields = 22.37%), whereas for CFr was dextrose (wet base yields = 601.49% and dry base yields = 28.14%). Finally, the MCFs produced by COr and CFr showed a homogeneous, thick appearance, slight flexibility, and the characteristic brown color of the fermentation medium.

We have evaluated the effect of edible coatings (ECs) based on linseed mucilage (LM), chitosan (CH), and their combination (LMCH) on the quality and shelf life of fresh-cut cantaloupe. Cantaloupe was washed, sanitized, and processed (peeled, seeded, and cut) and then coated by immersion, packed, and stored for 18 days at 4 °C. The ECs were effective at reducing the juice leakage and softening of the product. The EC based on CH was the most effective at preserving the color parameter and reducing the general microbiological growth. However, the LMCH combination decreased the antimicrobial effect of chitosan against microorganisms. Also, CH and LM ECs helped preserve the overall sensory characteristics, increasing the acceptance to 12–15 days. Finally, the LMCH combination helped preserve the characteristics of color and odor; however, it modified the texture and taste of fresh-cut cantaloupe and its sensory acceptance was similar to the control (up to 9 days).

The aim of this research was to develop and characterize five gelled double emulsions based on chia mucilage (CM) and different biopolymers (κ-carrageenan, C; locust bean gum, L; thixogum, T; and whey protein concentrate, W) loaded with green tea extract (GTE). Gelled double emulsions consisted of W₁ (whey-protein-concentrate/sodium-azide/NaCl/GTE)/O and (PGPR/canola-oi)/W₂ (CM, CMC, CML, CMT and CMW), and were characterized based on physicochemical properties during 35 days of storage. Optical microscopy clearly showed the drops of the internal phase surrounded by droplets of oil dispersed in the second aqueous phase; the droplet size was higher for CMT and lowest for CMW. In addition, all emulsions were highly stable at creaming and were effective in reducing the loss of antioxidant activity (88.82%) and total phenols (64.26%) during storage; CMT, CML and CM were the most effective. Furthermore, all emulsions showed a protective effect by modulating the release of the GTE in a simulated gastrointestinal environment, allowing a controlled release during the gastric-intestinal digestion phases and reaching its maximum release in the intestinal phase (64.57–83.31%). Thus, gelled double emulsions are an alternative for the preservation of GTE and could be a potential alternative for their application in the development of functional foods.

The purpose of this research is to produce and characterize bacterial cellulose (BC) films coated with chitosan (BC-CH). BC films were produced in a fermentation medium based on Camellia sinensis tea and dextrose (12 days at 25 °C) and subsequently treated with coating-forming solutions (CFSs) based on chitosan (BC-CH 0.5%, BC-CH 1.0%, and BC-CH 1.5%). As a result, the FTIR spectra of BC and BC-CH 1.5% showed the main characteristic bands of cellulose and chitosan. In the physicochemical characterization of the films, it was found that the incorporation of the chitosan coatings did not affect the thickness; however, it decreased the luminosity (L*) and increased redness (a*), yellowness (b*), and opacity (75.24%). Additionally, the light absorption properties in the UV-Vis range were improved. Furthermore, the application of the CFSs increased: the solubility (64.91%), the antimicrobial activity against S. aureus (6.55 mm) and E. coli (8.25 mm), as well as the antioxidant activity (57.71% and 24.57% free radical scavenging activity), and the content of total phenols (2.45 mg GAE/g). Finally, our results suggest that the BC-CH films developed in the present study show a potential application as active packaging material for food.