Vegetation growing recycled concrete (VGRC) is a relatively new building material that has both biocompatibility and engineering function. The basic performance of VGRC was investigated by experimental analysis, and the hydration products and pore structure of different VGRC mix proportions were studied by X-ray diffraction (XRD), scanning electron microscope (SEM), and industrial computed tomography (CT). The results show that ultrafine slag can reduce Ca(OH)₂ content in cementing material and has a filling effect on micropores. VGRC has the best performance; the internal pore distribution is uniform when porosity is 20–25%, and the ultrafine slag content is 40%. The compressive strength of VGRC is greatly damaged by the quick-freezing method, while the degree of damage from natural freeze–thaw cycles is relatively small. Soaking in acid solution can effectively reduce the internal pore alkalinity of VGRC. Most plants can grow normally in vegetation concrete, and plant roots can penetrate 6-cm thick concrete blocks after being planted for 60 days. The compressive strength of VGRC decreased after turf planting of 30 days and then increased slowly. The permeability coefficient of VGRC increases with the increase in porosity and aggregate size and decreases after planting and covering. The frost resistance of VGRC is enhanced, and the influence of aggregate size and porosity is small after turf planting.

This paper aims to study the effectiveness of adding waste polypropylene fibers into recycled aggregate concrete (RAC) on shrinkage cracking. The influences of fiber properties (length and content) on the shrinkage performance of RAC are investigated. Firstly, through the plat-ring-type shrinkage test and free shrinkage test, both of the early age and long-term shrinkage performance of waste fiber recycled concrete (WFRC) were measured. Then, X-ray industrial computed tomography (ICT) was carried out to reflect the internal porosity changes of RAC with different lengths and contents of fibers. Furthermore, the compressive strength and flexural strength tests are conducted to evaluate the mechanical performance. The test results indicated that the addition of waste fibers played an important role in improving the crack resistance performance of the investigated RAC specimens as well as controlling their shrinkage behaviour. The initial cracking time, amount and width of cracks and shrinkage rate of fiber-reinforced specimens were better than those of the non-fiber-reinforced specimen. The addition of waste fibers at a small volume fraction in recycled concrete had not obviously changed the porosity, but it changed the law of pore size distribution. Meanwhile, the addition of waste fibers had no significant effect on the compressive strength of RAC, but it enhanced the flexural strength by 43%. The specimens reinforced by 19-mm and 0.12% (volume fraction) waste fibers had the optimal performance of cracking resistance.

A study was undertaken to investigate the effects of crumb rubber on the strength and mechanical behaviour of Rubberized cement soil (RCS). In the present investigation, 26 groups of soil samples were prepared at five different percentages of crumb rubber content, four different percentages of cement content and two different finenesses of crumb rubber particle. Compressive strength tests were carried out at the curing age of 7 days, 14 days, 28 days and 90 days. The test results indicated that the inclusion of crumb rubber within cement soil leads to a decrease in the compressive strength and stiffness and improves the cement soil’s brittle behaviour to a more ductile one. A reduction of up to 31% in the compressive strength happened in the 20% crumb content group. The compressive strength increases with the increase in the cement content. And the enlargement of cement content is more efficient at low cement content.

AC (asphalt concrete)-13, as the main material used in pavement construction, has been applied widely in seasonal frozen areas. In order to understand the fracture mechanism in the freeze-thaw (F-T) damage process, the mesoscale structure of AC-13 is obtained by computed tomography (CT). The fractal dimension of cracks is used as a damage evaluation index. Most previous studies have only focused on the fractal dimensions of whole cracks, while ignoring the fractal tectonic process and the self-similarity degree of a single fracture. Therefore, in this study, the intrinsic mechanism of fractures and damage were investigated. In addition, the critical crack stress and fracture toughness models of a single fracture in a freeze-thaw damage process are established for AC-13. The results indicate that in terms of the critical crack stress and fracture toughness, with the increase of F-T times, there is an obvious decreasing trend. The fracture model can effectively describe the fracture toughness calculated by ABAQUS in the process of freeze-thaw cycles.

Natural aeolian sand has the characteristics of low cohesion and poor water stability. In order to improve its crack resistance properties in the process of freeze-thaw cycles, P.O 42.5 ordinary Portland cement was added to form a mixture called cement improved aeolian sand (CIAS). SEM was used to analyze the microscopic micro-structure of CIAS at different times (7 days and 28 days). The mechanical properties of CIAS samples affected by freeze-thaw cycles were tested in a triaxial instrument, and gray-scale images of the three-phase distribution in the CIAS after freeze-thaw cycling were obtained by computed tomography (CT) scanning technology. The pore characteristic parameters (pore area, fractal dimension, and crack length) were studied by digital image process technique. Based on classical Griffith fracture theory, the development of the crack length and crack width with increasing freeze-thaw cycles is determined. Assuming that the pore area subordinates to the Weibull distribution, the parameters of the Weibull distribution, the damage evolution defined by the elastic modulus attenuation, and the pore area development of CIAS were determined. Research shows the cohesion decreases and internal friction angle increases with increasing cycle numbers. Three development patterns are observed: crack growth, crack closure, and crack merging, and the three patterns interact during freeze-thaw cycling. Furthermore, the fractal dimension of the pore edge fluctuates with the increasing number of freeze-thaw cycles. This work provides a theoretical basis for the application of aeolian sand and develops a method for disaster prevention in applications of freeze-thaw cycling.