AC (asphalt concrete)-13, as the main material used in pavement construction, has been applied widely in seasonal frozen areas. In order to understand the fracture mechanism in the freeze-thaw (F-T) damage process, the mesoscale structure of AC-13 is obtained by computed tomography (CT). The fractal dimension of cracks is used as a damage evaluation index. Most previous studies have only focused on the fractal dimensions of whole cracks, while ignoring the fractal tectonic process and the self-similarity degree of a single fracture. Therefore, in this study, the intrinsic mechanism of fractures and damage were investigated. In addition, the critical crack stress and fracture toughness models of a single fracture in a freeze-thaw damage process are established for AC-13. The results indicate that in terms of the critical crack stress and fracture toughness, with the increase of F-T times, there is an obvious decreasing trend. The fracture model can effectively describe the fracture toughness calculated by ABAQUS in the process of freeze-thaw cycles.

Experimental studies on reinforcing aeolian sand with cement and fiber are lacking, and the interface mechanism and splitting characteristics thus remain unclear. Herein, the interface mechanism and splitting characteristics of fiber-reinforced, cement-solidified, aeolian sand were experimentally assessed to investigate whether glass fiber exhibits better properties as a reinforcing agent than traditional fiber-free cement-solidified aeolian sand, and whether aeolian sand is applicable as a base material in geotechnical engineering. The splitting experiments involved the use of fiber-reinforced, cement-solidified aeolian sand samples that were differentiated based on the mixing schemes used to formulate them. Based on the strengthening control technology effects on the structural performance of the fiber-reinforced, cement aeolian, sand-mixed matrix material, the internal physical and chemical mechanisms of structural performance evolution were revealed and analyzed using scanning electron microscopy images. The experimental results show that the splitting strength of the sample reaches its maximum value at a combination of 6 mm glass fiber, 3‰ fiber, and 10% cement contents. In fiber-reinforced cement-solidified aeolian sand, cement hydrate forms more needle-shaped crystal products. The crystals adhere to the fiber surfaces that interweave with each other to form a porous and dense network. Although this improves the bonding force between the fiber and aeolian sand particles, the fibers are prone to fracture and slippage during the splitting process. The three-dimensional network structure formed by overlapping fibers is critical for the improvement of the splitting strength. The study’s findings will serve as benchmarks to achieve additional improvements in glass fiber-reinforced cement-solidified aeolian sand.

Natural aeolian sand has the characteristics of low cohesion and poor water stability. In order to improve its crack resistance properties in the process of freeze-thaw cycles, P.O 42.5 ordinary Portland cement was added to form a mixture called cement improved aeolian sand (CIAS). SEM was used to analyze the microscopic micro-structure of CIAS at different times (7 days and 28 days). The mechanical properties of CIAS samples affected by freeze-thaw cycles were tested in a triaxial instrument, and gray-scale images of the three-phase distribution in the CIAS after freeze-thaw cycling were obtained by computed tomography (CT) scanning technology. The pore characteristic parameters (pore area, fractal dimension, and crack length) were studied by digital image process technique. Based on classical Griffith fracture theory, the development of the crack length and crack width with increasing freeze-thaw cycles is determined. Assuming that the pore area subordinates to the Weibull distribution, the parameters of the Weibull distribution, the damage evolution defined by the elastic modulus attenuation, and the pore area development of CIAS were determined. Research shows the cohesion decreases and internal friction angle increases with increasing cycle numbers. Three development patterns are observed: crack growth, crack closure, and crack merging, and the three patterns interact during freeze-thaw cycling. Furthermore, the fractal dimension of the pore edge fluctuates with the increasing number of freeze-thaw cycles. This work provides a theoretical basis for the application of aeolian sand and develops a method for disaster prevention in applications of freeze-thaw cycling.

This paper puts forward a new soft soil reinforcement technology—microbial-induced calcite precipitation (MICP) technology—which considers the problem of dredger fill soft-soil reinforcement in Dalian Taiping Bay. In this paper, the calcium carbonate content (CCC) and unconfined compressive strength (UCS) of microbial solidified dredger fill (MSDF) samples were determined using laboratory experiments. The microstructure and chemical composition of MSDF samples were studied by SEM–EDS and XRD. The failure and reinforcement mechanism of MSDF under different experimental conditions (ambient temperature, cementation solution concentration, and clay content) were investigated. The results showed that there was a certain residual strength after the peak strength of MSDF. With the increase of ambient temperature, the number of microorganisms increased, but the activities of urease, CCC, and UCS decreased. The UCS and CCC increased with the increase of cementation solution concentration, while they first increased and then decreased with the increase of clay content. The clay content enhanced the compactness of MSDF samples but reduced the soil permeability and weakened the mineralization. There were significant differences in the morphology of microbial-induced precipitation caused by different concentrations of cementation solution.

In order to improve the availability of waste rubber tires and bearing capacity of sand foundation, a new composite foundation transforms the tensile strength of a discarded rubber tire into a hoop-tightening force on granular sand soil, i.e. hoop capacity, is introduced and investigated. Considering the characteristics of the circular enclosed structure of the tire, the tensile strength of the tire strips was obtained by carrying out a tension test of tire strips, and the relationships between earth pressure, settlement and vertical load were discovered by the results of loading tests under the conditions of confined and unconfined. The distribution of circumferential stress at each position of the tire cross section was monitored to evaluate the contribution of each part of the tire to the integral hoop capacity. Based on the theory of annular elasticity, Airy stress-state function is introduced to determine the solutions of stress, strain and displacement in the sand and tire regions based on the stress boundary condition and displacement continuity condition. The results show that the theory prediction curve has a high precision approaching the measured data, which indicates the rationality of the proposed theoretical model in predicting the circumferential stress of this type of waste rubber tire composite foundations.

In order to study the influence of freeze–thaw cycles on chloride ion corrosion resistance of RPC with copper slag (CS) instead of quartz sand (QS), the 28d uniaxial compressive strength (UCS) of CSRPC with a different CS substitution rate was investigated by unconfined compression tests. The electric flux test method was used to study the chloride ion diffusion resistance of CSRPC after freeze–thaw cycles, and the pore size distribution was obtained through the nuclear magnetic resonance (NMR) method. Then, a mathematical relationship between the chloride ion diffusion coefficient and the pore fractal characteristic parameter T was established to study the effect of freeze–thaw cycles on chloride ion diffusion. Finally, SEM/EDS, XRD, and DTG methods were combined to study the influence of the distribution of Friedel’s salts generated after freeze–thaw cycles on chloride ion diffusion in CSRPC. The results indicate that CS has a micro aggregate effect and pozzolanic activity, which can effectively improve the chloride ion diffusion resistance of CSRPC after freeze–thaw cycles. In addition, the electric flux of CSRPC decreases with the increase in freeze–thaw cycles, and the chloride diffusion coefficient is closely related to the pore fractal dimension.