The effect of temperature (from 288 to 308 K) and concentration of sulfide ions (up to 40 ppm) on the corrosion behavior of AISI 304L and AISI 316L stainless steels in seawater was studied with measurements of open-circuit potential, linear and potentiodynamic polarization, and electrochemical impedance spectroscopy. An increase in temperature and pollutant concentration negatively affects the corrosion stability of stainless steels at the open circuit (the resistance, compactness, and thickness of the surface layer decrease and the corrosion current increases), in the passive region (the passivation current increases, the depassivation potential decreases, and the passive potential region narrows), and in the transpassive potential region (the rate of metal dissolution increases). The occurrence of pitting corrosion on the surface of the samples was confirmed with optical microscopy and a non-contact 3D profilometer. A few large pits (depth 80–100 μm and width 100 μm) were formed on the surface of AISI 304L steel, while several smaller pits (depth 40–50 μm and width 50 μm) were formed on the surface of AISI 316L steel. With increasing temperature and sulfide ion concentration, the width, depth, and density of the pits increased on both steel samples. In the studied temperature and concentration range of sulfide ions, the AISI 316L steels exhibited higher corrosion resistance. Overall, the influence of sulfide ions on steel corrosion was more pronounced than the influence of temperature.

The main aim of this paper is to present an environmentally friendly method for aluminum recycling. Development of new recycling technologies in order to increase scrap reuse potential and CO₂ emission savings are of the main importance for aluminum circular economy. In this paper, aluminum chips waste was recycled without any remelting phase in order to increase energy and material savings. The presented process is usually called solid state recycling or direct recycling. Solid state recycling process consists of chips cleaning, cold pre-compaction and hot direct extrusion followed by a combination of equal channel angular pressing (ECAP) and heat treatment. Influence of holding time during solid solution treatment and both artificial aging time and temperature on mechanical properties of the recycled EN AW 6082 aluminum chips were investigated. A comprehensive number of the experiments were performed utilizing design of experiments approach and response surface methodology. Regression models were developed for describe the influence of heat treatment parameters for presented solid state recycling process on mechanical properties of the recycled samples. Utilizing novel procedure high quality recycled samples were obtained with mechanical properties comparable with commercially produced EN AW 6082 aluminum alloy in T6 temper condition. Metallographic analysis of the recycled samples was also performed.

Ti and Ti6Al4V alloy are extensively utilized in structural parts in engineering applications and the production of medical implants due to their excellent mechanical properties, lightweight, and high corrosion resistance. This study comprehensively evaluates their corrosion behavior in three challenging aquatic environments: brackish water, seawater, and seawater bittern. Utilizing open circuit potential (E_OC) measurements with polarization techniques (linear and potentiodynamic) and electrochemical impedance spectroscopy (EIS) measurements, the research highlights distinct environmental influences on corrosion performance. Notably, Ti and Ti6Al4V alloy demonstrated exceptional stability with the highest polarization resistance and lowest corrosion current in brackish water, while seawater bittern presented the most demanding condition for Ti6Al4V. Additionally, the analysis of the electrode surfaces after polarization measurements using optical microscopy, optical profilometry, and SEM/EDS tests revealed minor damage, indicating the high corrosion resistance of these materials. This study advances the understanding of Ti and Ti6Al4V alloy performance in diverse environments and offers valuable insights for optimizing their use in harsh aquatic conditions, particularly for applications requiring durability and longevity.