Objective: To determine whether engineered cartilage generated by nasal chondrocytes (ECN) is responsive to different regimens of loading associated with joint kinematics and previously shown to be stimulatory of engineered cartilage generated by articular chondrocytes (ECA).Methods: Human nasal and articular chondrocytes, harvested from 5 individuals, were expanded and cultured for 2 weeks into porous polymeric scaffolds. The resulting ECN and ECA were then maintained under static conditions or exposed to the following loading regimens: regimen 1, single application of cyclic deformation for 30 minutes; regimen 2, intermittent application of cyclic deformation for a total of 10 days, followed by static culture for 2 weeks; regimen 3, application of surface motion for a total of 10 days.Results: Prior to loading, ECN constructs contained significantly higher amounts of glycosaminoglycan (GAG) and type II collagen compared with ECA constructs. ECN responded to regimen 1 by increasing collagen and proteoglycan synthesis, to regimen 2 by increasing the accumulation of GAG and type II collagen as well as the dynamic modulus, and to regimen 3 by increasing the expression of superficial zone protein, at the messenger RNA level and the protein level, as well as the release of hyaluronan. ECA constructs were overall less responsive to all loading regimens, likely due to the lower extracellular matrix content.Conclusion: Human ECN is responsive to physical forces resembling joint loading and can up‐regulate molecules typically involved in joint lubrication. These findings should prompt future in vivo studies exploring the possibility of using nasal chondrocytes as a cell source for articular cartilage repair.

Repeated passaging in conventional cell culture reduces pluripotency and proliferation capacity of human mesenchymal stem cells (MSC). We introduce an innovative cell culture method whereby the culture surface is dynamically enlarged during cell proliferation. This approach maintains constantly high cell density while preventing contact inhibition of growth. A highly elastic culture surface was enlarged in steps of 5% over the course of a 20-day culture period to 800% of the initial surface area. Nine weeks of dynamic expansion culture produced 10-fold more MSC compared with conventional culture, with one-third the number of trypsin passages. After 9 weeks, MSC continued to proliferate under dynamic expansion but ceased to grow in conventional culture. Dynamic expansion culture fully retained the multipotent character of MSC, which could be induced to differentiate into adipogenic, chondrogenic, osteogenic, and myogenic lineages. Development of an undesired fibrogenic myofibroblast phenotype was suppressed. Hence, our novel method can rapidly provide the high number of autologous, multipotent, and nonfibrogenic MSC needed for successful regenerative medicine.

This study aimed at testing whether an RGD-restricted substrate interface is sufficient for adhesion and growth of human articular chondrocytes (HAC), and whether it enhances their post expansion chondrogenic capacity. HAC/substrate interaction was restricted to RGD by modifying tissue culture polystyrene (TCPS) with a poly(ethylene glycol) (PEG) based copolymer system that renders the surface resistant to protein adsorption while at the same time presenting the bioactive RGD-containing peptide GCRGYGRGDSPG (RGD). As compared to TCPS, HAC cultured on RGD spread faster (1.9-fold), maintained higher type II collagen mRNA expression (4.9-fold) and displayed a 19% lower spreading area. On RGD, HAC attachment efficiency (66±10%) and proliferation rate (0.56±0.04 doublings/day), as well as type II collagen mRNA expression in the subsequent chondrogenic differentiation phase, were similar to those of cells cultured on TCPS. In contrast, cartilaginous matrix deposition by HAC expanded on RGD was slightly but consistently higher (15% higher glycosaminoglycan-to-DNA ratio). RDG (bioinactive peptide) and PEG (no peptide ligand) controls yielded drastically reduced attachment efficiency (lower than 11%) and proliferation (lower than 0.20 doublings/day). Collectively, these data indicate that restriction of HAC interaction with a substrate through RGD peptides is sufficient to support their adhesion, growth and maintenance of cartilage forming capacity. The concept could thus be implemented in materials for cartilage repair, whereby in situ recruited/infiltrated chondroprogenitor cells would proliferate while maintaining their ability to differentiate and generate cartilage tissue.

The provision of mechanical stimulation is believed to be necessary for the functional assembly of skeletal tissues, which are normally exposed to a variety of biomechanical signals in vivo. In this paper, we present a development and validation of a novel bioreactor aimed for skeletal tissue engineering that provides dynamic compression and perfusion of cultivated tissues. Dynamic compression can be applied at frequencies up to 67.5 Hz and displacements down to 5 ?m thus suitable for the simulation of physiological conditions in a native cartilage tissue (0.1-1 Hz, 5-10 % strain). The bioreactor also includes a load sensor that was calibrated so to measure average loads imposed on tissue samples. Regimes of the mechanical stimulation and acquisition of load sensor outputs are directed by an automatic control system using applications developed within the LabView platform. In addition, perfusion of tissue samples at physiological velocities (10-100 ?m/s) provides efficient mass transfer, as well as the possibilities to expose the cells to hydrodynamic shear and simulate the conditions in a native bone tissue. Thus, the novel bioreactor is suited for studies of the effects of different biomechanical signals on in vitro regeneration of skeletal tissues, as well as for the studies of newly formulated biomaterials and cell biomaterial interactions under in vivo-like settings.

Stratum corneum, the outermost layer of skin, allows transport of only low-molecular weight ( 2,000, exhibit skin permeabilities comparable to those of small hydrophobic molecules, such as estradiol. Systematic fragmentation of the Av molecule shows that deletion of the outer monoterpene results in a 62% reduction in permeability, suggesting an important role for this motif in skin permeation. Further removal of the tetrasaccharide residue results in a further reduction of permeability by 79%. These results, taken in sum, imply that synergistic effects involving both hydrophobic and hydrophilic residues may hold the key in facilitating translocation of Av s across skin lipids. In addition to exhibiting high permeability, Av s provided moderate enhancements of skin permeability of estradiol and polysaccharides, including dextran and inulin but not polyethylene glycol.